Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance, good mold flow.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.87 g/cc
1.87 g/cc
at 25°C
Oxygen Transmission 118 cc-mm/m²-24hr-atm
300 cc-mil/100 in²-24hr-atm
Nitrogen Transmission 48.0 cc-mm/m²-24hr-atm
122 cc-mil/100 in²-24hr-atm
Carbon Dioxide Transmission 109 cc-mm/m²-24hr-atm
277 cc-mil/100 in²-24hr-atm
Mooney Viscosity 19

@Temperature 121 °C
19

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
Peak value, at 25°C
Tensile Strength at Break 22.0 MPa
3190 psi
Tensile Strength, Yield 3.10 MPa

@Strain 100 %
450 psi

@Strain 100 %
Elongation at Break 330 %
330 %
Tear Strength 19.6 kN/m
112 pli
at 25°C
Taber Abrasion, mg/1000 Cycles 150
150
H-22 abrasive wheel, load: 1000g x 2
Compression Set 13 %
13 %
70 hours at 25°C
12 %

@Temperature 100 °C
12 %

@Temperature 212 °F
70 hours
15 %

@Temperature 175 °C
15 %

@Temperature 347 °F
70 hours
28 %

@Temperature 200 °C
28 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -8.00 °C
17.6 °F
TR test, TR10
-5.00 °C
23.0 °F
Gehman torsion test, T10
-2.00 °C
28.4 °F
TR test, TR70
-1.30 °C
29.7 °F
Gehman torsion test, T2
Brittleness Temperature -26.0 °C
-14.8 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Processing Properties Metric English Comments
Processing Temperature 160 °C
320 °F
Cure Measuring Temperature
Cure Time 2.60 min
0.0433 hour
Curelastmeter