Material Notes:
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had defects in terms of moldability, thermal stability, and impact resistance.ApplicationsMobile phonesvehicle-mounted audio equipmentautomotive interior componentshome electric appliancesOA equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 265 °C
20 g/10 min

@Load 22.0 lb,
Temperature 509 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ISO 2039-2
114
114
ASTM D785
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D638
41.0 MPa
5950 psi
50mm/min; ISO 527-2
Tensile Strength, Yield 38.0 MPa
5510 psi
ISO 527-2
Elongation at Break 21 %
21 %
ISO 527-2
Tensile Modulus 2.20 GPa
319 ksi
1mm/min; ISO 527-1
Flexural Strength 70.0 MPa
10200 psi
ISO 178
71.0 MPa
10300 psi
15mm/min; ASTM D790
Flexural Modulus 2.05 GPa
297 ksi
15mm/min; ASTM D790
2.10 GPa
305 ksi
2mm/min; ISO 178
Izod Impact, Notched 1.57 J/cm

@Temperature 23.0 °C
2.94 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
ISO 75-2
118 °C
244 °F
ASTM D648
Vicat Softening Point 131 °C
268 °F
50N; ISO 306
Flammability, UL94 HB
HB