Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene

Category Polymer , Thermoplastic , Styrene-Butadiene
Manufacturer Denka
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a good balance of transparency, strength and fluidity (methyl methacrylate butadiene styrene), "TE Series/CL Series," transparent ABS resins with excellent color attributes and tensile strength are available (among others).ApplicationsTX is used for:flat display substratesoptical componentsmiscellaneous goods.TP/TH are used for:food package sheeting as well as in manufacturingelectronic equipment and componentsmiscellaneous goodsTE/CL are for:electronic equipment and componentsinformation equipment componentsAV equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.082 g/cc
0.03909 lb/in³
ISO 1183
Melt Flow 5.1 g/10 min

@Load 5.00 kg,
Temperature 200 °C
5.1 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
59 g/10 min

@Load 10.0 kg,
Temperature 220 °C
59 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 29
29
ISO 2039-2
Tensile Strength at Break 34.0 MPa
4930 psi
50mm/min; ISO 527-2
39.0 MPa
5660 psi
50mm/min; ASTM D638
Elongation at Break 40 %
40 %
50mm/min; ISO 527-2
Tensile Modulus 4.40 GPa
638 ksi
50mm/min; ISO 527-1
Flexural Strength 65.0 MPa
9430 psi
2mm/min; ASTM D790
65.0 MPa
9430 psi
ISO 178
Flexural Modulus 2.05 GPa
297 ksi
2mm/min; ASTM D790
2.10 GPa
305 ksi
2mm/min; ISO 178
Izod Impact Resistance 12.6 J/cm²
60.0 ft-lb/in²
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
ISO 75-2
71.0 °C
160 °F
ASTM D648
Vicat Softening Point 84.0 °C
183 °F
50N; ISO 306
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Haze 2.7 %

@Thickness 2.00 mm
2.7 %

@Thickness 0.0787 in
ISO 14782
Transmission, Visible 91 %

@Thickness 2.00 mm
91 %

@Thickness 0.0787 in
ISO 13468-1