Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Diamond Polymers ASA S950

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ASA S950.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 0.80 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.80 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 Procedure A Condition G; ASTM D1238
2.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 2.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 Procedure A Condition I; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 87
87
ASTM D785
Tensile Strength, Yield 35.9 MPa
5200 psi
chs 2 in/min; ASTM D638
Flexural Modulus 1.61 GPa
233 ksi
Tangent, chs 0.05 in/min; ASTM D790
Izod Impact, Notched 4.27 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 8.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 bar; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
91.1 °C
196 °F
0.125 in bar Annealed 4 hours at 80°C; ASTM D648
Vicat Softening Point 104 °C
219 °F
0.125 inch, 1 Kg; ASTM D1525