Diamond Polymers Centrex® 810 Injection Molding Grade

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Diamond and Network Polymers
Trade Name Centrex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers Centrex® 810 Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Centrex 810 resin is a soft-flow, high-gloss, and medium-impact grade of ASA (acrylonitrile-styrene-acrylate). It is an injection molding grade with a good balance of physical properties, gloss and processing performance, along with good resistance to weather aging. As with any product, use of Centrex 810 resin must be tested (including field testing, etc.) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ASTM D955
Melt Flow 21 g/10 min

@Load 10.0 kg,
Temperature 220 °C
21 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength, Yield 40.7 MPa
5900 psi
chs 2.0 in/min; ASTM D638
Tensile Modulus 2.46 GPa
357 ksi
chs 2.0 in/min; ASTM D638
Flexural Strength 70.3 MPa
10200 psi
chs 0.05 in/min; ASTM D790
Flexural Modulus 2.39 GPa
347 ksi
tangent; chs 0.05 in/min; ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
1.00 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
ASTM D256
0.641 J/cm

@Thickness 3.17 mm,
Temperature 0.000 °C
1.20 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
ASTM D256
0.854 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
1.60 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Impact Test 10.0 J

@Temperature -30.0 °C
7.38 ft-lb

@Temperature -22.0 °F
ASTM D3763
40.0 J

@Temperature 0.000 °C
29.5 ft-lb

@Temperature 32.0 °F
ASTM D3763
45.0 J

@Temperature 23.0 °C
33.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
0.125";; ASTM D648
80.0 °C
176 °F
0.25";; ASTM D648
Vicat Softening Point 104 °C

@Load 1.00 kg
219 °F

@Load 2.20 lb
120°C/hr; ASTM D1525
93.0 °C

@Load 5.00 kg,
Thickness 1270 mm
199 °F

@Load 11.0 lb,
Thickness 50.0 in
ASTM D1525