Diamond Polymers Centrex® 813 General Purpose Injection Molding Grade ASA/AES

Category Polymer , Thermoplastic , AES Polymer , ASA Polymer , ASA/AES, Unreinforced, Extruded/Molded
Manufacturer Diamond and Network Polymers
Trade Name Centrex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers Centrex® 813 General Purpose Injection Molding Grade ASA/AES.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Centrex 813 resin is a high-gloss, high-impact grade of ASA/AES, a blend of acrylonitrile-styrene-acrylate and acrylonitrile-ethylene-propylene styrene. This injection molding grade with a good balance of physical properties and processing performance, along with good resistance to weather aging. It also features excellent low-temperature multiaxial impact strength.Applications: Centrex 813 resin is used in lawn and garden tractor components; boat and marine accessory parts; large, outdoor TV screen displays; pool accessories, covers, and filter housings. As with any product, use of Centrex 813 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ASTM D955
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 85
85
ASTM D785
Tensile Strength, Yield 34.0 MPa
4930 psi
chs 2.0 in/min; ASTM D638
Tensile Modulus 2.00 GPa
290 ksi
chs 2.0 in/min; ASTM D638
Flexural Strength 54.0 MPa
7830 psi
chs 0.05 in/min; ASTM D790
Flexural Modulus 1.929 GPa
279.8 ksi
tangent; chs 0.05 in/min; ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 3.17 mm,
Temperature -40.0 °C
0.993 ft-lb/in

@Thickness 0.125 in,
Temperature -40.0 °F
ASTM D256
3.90 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
7.31 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Impact Test 22.0 J

@Temperature -40.0 °C
16.2 ft-lb

@Temperature -40.0 °F
ASTM D3763
33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
0.125";; ASTM D648
77.0 °C
171 °F
0.5";; ASTM D648
Vicat Softening Point 101 °C

@Load 1.00 kg
214 °F

@Load 2.20 lb
120°C/hr; ASTM D1525
Flammability, UL94 HB

@Thickness 15.0 mm
HB

@Thickness 0.590 in