Diamond Polymers DIAMALOY GLY 7010 Sheet Extrusion Grade

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers DIAMALOY GLY 7010 Sheet Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Diamaloy GLY 7010 resin is a high-gloss, high impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, and it can be easily coextruded.Applications: Typical applications include those requiring weatherability and high impact such as in pool and spa applications. As with any product, use of Diamaloy GLY 7010 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0050 cm/cm
0.0040 - 0.0050 in/in
ASTM D955
Melt Flow 3.5 g/10 min

@Load 5.00 kg,
Temperature 260 °C
3.5 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
3.7 g/10 min

@Load 10.0 kg,
Temperature 220 °C
3.7 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 91
91
ASTM D785
Tensile Strength at Break 35.0 MPa
5080 psi
chs 2.0 in/min; ASTM D638
Tensile Strength, Yield 42.0 MPa
6090 psi
chs 2.0 in/min; ASTM D638
Elongation at Break 40 %
40 %
chs 2.0 in/min; ASTM D638
Elongation at Yield 3.2 %
3.2 %
chs 2.0 in/min; ASTM D638
Tensile Modulus 1.922 GPa
278.8 ksi
chs 2.0 in/min; ASTM D638
Flexural Strength 60.0 MPa

@Thickness 3.17 mm
8700 psi

@Thickness 0.125 in
chs 0.05 in/min; 2 in span; ASTM D790
Flexural Modulus 1.922 GPa

@Thickness 3.17 mm
278.8 ksi

@Thickness 0.125 in
chs 0.05 in/min; 2 in span; ASTM D790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
2.00 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
ASTM D256
4.81 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
9.01 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Impact Test 16.8 J

@Temperature -30.0 °C
12.4 ft-lb

@Temperature -22.0 °F
Total Energy; ASTM D3763
24.2 J

@Temperature 23.0 °C
17.8 ft-lb

@Temperature 73.4 °F
Total Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature -40.0 - 37.8 °C
50.0 µin/in-°F

@Temperature -40.0 - 100 °F
ASTM E831
CTE, linear, Transverse to Flow 108 µm/m-°C

@Temperature -40.0 - 37.8 °C
60.0 µin/in-°F

@Temperature -40.0 - 100 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
0.125";; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
0.125";; ASTM D648
Vicat Softening Point 102 °C
216 °F
ASTM D1525
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0590 in
Optical Properties Metric English Comments
Gloss 95 %
95 %
Untextured; 60°; ASTM D523
Electrical Properties Metric English Comments
Hot Wire Ignition, HWI 3.0 sec
3.0 sec
PLC Code; ASTM 746A
High Amp Arc Ignition, HAI 0.00 arcs
0.00 arcs
PLC Code; ASTM 746A