Diamond Polymers NPP25-1001 TF20 20% Talc Filled Copolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 20% Talc Filler |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers NPP25-1001 TF20 20% Talc Filled Copolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ash | 18 - 22 % | 18 - 22 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | chs 2.0 in/min; ASTM D638 |
| Tensile Modulus | 1.723 GPa | 249.9 ksi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 39.3 MPa | 5700 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 1.757 GPa | 254.8 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm @Thickness 3.17 mm |
1.11 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Dart Drop, Total Energy | 5.20 J | 3.84 ft-lb | ASTM D5420 |