Dow AFFINITY™ PF 1146G Polyolefin Plastomer (POP)

Category Polymer , Film , Thermoplastic , Polyolefin
Manufacturer Dow Chemical
Trade Name AFFINITY™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AFFINITY™ PF 1146G Polyolefin Plastomer (POP).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AFFINITY™ PF 1140G Polyolefin Plastomer (POP) is produced via INSITE™ Technologies. It is designed for high speed packaging applications requiring low seal initiation temperature and good machinability.Information provided by Dow
Physical Properties Metric English Comments
Density 0.8996 g/cc
0.03250 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Antiblock Level 6000 ppm
6000 ppm
Slip Level 3500 ppm
3500 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 6.43 MPa
933 psi
ASTM D882
Film Tensile Strength at Yield, TD 5.98 MPa
868 psi
ASTM D882
Film Elongation at Break, MD 554 %
554 %
ASTM D882
Film Elongation at Break, TD 602 %
602 %
ASTM D882
Secant Modulus, MD 0.0510 GPa
7.40 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.0550 GPa
7.98 ksi
2% Secant; ASTM D882
Impact 11
11
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
116
116
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy 3.56 J
2.62 ft-lb
Dow Method
Coefficient of Friction <= 0.20
<= 0.20
1.0 mil sealant layer in a co-extruded film
Elmendorf Tear Strength MD 378 g
378 g
ASTM D1922
Elmendorf Tear Strength TD 461 g
461 g
ASTM D1922
Elmendorf Tear Strength, MD 7.44 g/micron
189 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 9.075 g/micron
230.5 g/mil
ASTM D1922
Film Tensile Strength at Break, MD 37.3 MPa
5410 psi
ASTM D882
Film Tensile Strength at Break, TD 42.12 MPa
6109 psi
ASTM D882
Heat Seal Strength Initiation Temperature 75.0 °C
167 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 95.0 °C
203 °F
Dow Method (DSC)
Vicat Softening Point 76.0 °C
169 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 5.5 %
5.5 %
ASTM D1003
Gloss 77 %
77 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
Clarity; ASTM D1746