Dow DMDA-8907 NT 7 High Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DMDA-8907 NT 7 High Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW DMDA-8904 NT 7 is produced using UNIPOL™ process technology. It is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. Information provided by Dow
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D792
ESCR 100% Igepal® 12 hour

@Temperature 50.0 °C
12 hour

@Temperature 122 °F
F<sub>50</sub>; Molded and tested in accordance with ASTM D4976; ASTM D1693
Melt Index of Compound 6.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 59
59
Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 22.8 MPa
3300 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield 26.9 MPa
3900 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 1100 %
1100 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 1.07 GPa
155 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength 84.0 kJ/m²
40.0 ft-lb/in²
Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 131 °C
268 °F
Dow Method (DSC)
Crystallization Temperature 118 °C
244 °F
Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi) 72.8 °C
163 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point 128 °C
262 °F
ASTM D1525
Brittleness Temperature <= -76.1 °C
<= -105 °F
Molded and tested in accordance with ASTM D4976; ASTM D746