Dow DOWLEX™ 2077G Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2077G Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Fast processing on narrow die gaps Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9215 g/cc | 0.03329 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 1200 ppm | 1200 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.15 MPa | 1617 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.84 MPa | 1717 psi | ASTM D882 |
| Film Elongation at Break, MD | 393 % | 393 % | ASTM D882 |
| Film Elongation at Break, TD | 605 % | 605 % | ASTM D882 |
| Secant Modulus, MD | 0.2034 GPa | 29.50 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.2358 GPa | 34.20 ksi | 2% Secant; ASTM D882 |
| Impact | 89 | 89 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method |
| 870 | 870 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 | |
| 984 | 984 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 266 g | 266 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 679 g | 679 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.09 g/micron | 332.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.415 g/micron | 848.75 g/mil | ASTM D1922 |
| Dart Drop Test | 163 g | 0.359 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.08 MPa | 5668 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.54 MPa | 3704 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 48 % | 48 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- NextGen Adhesives P907-13 Fiber Optic Adhesive
- Permabond LM012 Anaerobic Threadsealant
- SABIC Innovative Plastics Lexan® R9453 PC (Asia Pacific)
- IRPC Polimaxx Polene PE300N Polypropylene Wax
- Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- Hexcel® HexWeb® HRP/OX - 3/8 - 5.5 Fiberglass/Phenolic Honeycomb
- Polyplastics Duranex® 652SA Polybutylene Terephthalate (PBT), Low density, Low wear, Mineral filled
- Dow Corning DM3 Demulsifier
Copyright © lookpolymers.com All Rights Reserved