Dow LDPE 535I Low Density Polyethylene, Liner Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow LDPE 535I Low Density Polyethylene, Liner Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW LDPE 535I resin is a barefoot general purpose liner resin with medium clarity for medium modulus packaging applications. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 40 µm. Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
Thickness 40.0 microns
1.57 mil
Melt Flow 1.9 g/10 min

@Load 2.16 kg
1.9 g/10 min

@Load 4.76 lb
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 10.0 MPa
1450 psi
Molded property
Film Tensile Strength at Yield, MD 12.4 MPa
1800 psi
Film Tensile Strength at Yield, TD 12.6 MPa
1830 psi
Tensile Strength, Yield 12.4 MPa
1800 psi
Molded property
Film Elongation at Break, MD 420 %
420 %
Film Elongation at Break, TD 585 %
585 %
Elongation at Break 500 %
500 %
Molded value
Coefficient of Friction 1.0
1.0
Elmendorf Tear Strength MD 145 g
145 g
Elmendorf Tear Strength TD 210 g
210 g
Elmendorf Tear Strength, MD 3.60 g/micron
91.4 g/mil
Elmendorf Tear Strength, TD 5.30 g/micron
135 g/mil
Dart Drop 1.60 g/micron
40.6 g/mil
Film Tensile Strength at Break, MD 26.7 MPa
3870 psi
Film Tensile Strength at Break, TD 19.5 MPa
2830 psi
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
Gloss 50 %
50 %
45°
Processing Properties Metric English Comments
Processing Temperature 177 °C
351 °F
Film extrusion temperature