Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Dow Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW LDPE 609A resin is a fully formulated high strength clarity film resin for optical packaging applications, such as produce and bakery film. It contains medium levels of slip additive and low levels of antiblock additive. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 30 µm. Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
Thickness 30.0 microns
1.18 mil
Melt Flow 0.90 g/10 min

@Load 2.16 kg
0.90 g/10 min

@Load 4.76 lb
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.9 MPa
1730 psi
Film Tensile Strength at Yield, TD 12.1 MPa
1750 psi
Film Elongation at Break, MD 310 %
310 %
Film Elongation at Break, TD 590 %
590 %
Coefficient of Friction 0.20
0.20
Elmendorf Tear Strength MD 370 g
370 g
Elmendorf Tear Strength TD 240 g
240 g
Elmendorf Tear Strength, MD 12.3 g/micron
312 g/mil
Elmendorf Tear Strength, TD 8.00 g/micron
203 g/mil
Dart Drop 2.70 g/micron
68.6 g/mil
Film Tensile Strength at Break, MD 24.1 MPa
3500 psi
Film Tensile Strength at Break, TD 19.8 MPa
2870 psi
Optical Properties Metric English Comments
Haze 4.4 %
4.4 %
Gloss 75 %
75 %
45°
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Processing Properties Metric English Comments
Processing Temperature 193 °C
379 °F
Film extrusion temperature