Dow Nordel® IP 5565 ASTM D3568
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 5565 ASTM D3568.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 5565
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 63 @Temperature 100 °C |
63 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 10.7 MPa | 1550 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 301 % | 301 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00190 GPa | 0.276 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00400 GPa | 0.580 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00780 GPa | 1.13 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0103 GPa | 1.49 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 26.0 kN/m | 148 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 60 % @Temperature 125 °C |
60 % @Temperature 257 °F |
Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -41.0 °C | -41.8 °F | Temperature Retraction, TR-10 |