Dow TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name TUFLIN™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Industrial pallet wrap stretch film applications Premium film packaging applications Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a TUFLIN™ HSE-1003 NT 7 is an ethylene-hexene-1 copolymer, designed for cast stretch film applications such as industrial pallet wrap. Films containing HSE-1003 offer outstanding puncture, toughness and load holding properties.Information provided by Dow
Physical Properties Metric English Comments
Density 0.9178 g/cc
0.03316 lb/in³
ASTM D792
Thickness 20.3 microns
0.800 mil
Melt Flow 2.45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.22 MPa
1628 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.5 MPa
1530 psi
ASTM D882
Film Elongation at Break, MD 519 %
519 %
ASTM D882
Film Elongation at Break, TD 828 %
828 %
ASTM D882
Elongation at Break 332 %
332 %
on-pallet testing: Ultimate Stretch; Highlight Industries Method
Secant Modulus, MD 0.1474 GPa
21.38 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.1557 GPa
22.58 ksi
2% Secant; ASTM D882
Impact 9.0
9.0
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
319
319
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
2524
2524
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
3246
3246
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Puncture Energy 3.84 J
2.83 ft-lb
Dow Method
Elmendorf Tear Strength MD 184 g
184 g
Method B; ASTM D1922
Elmendorf Tear Strength TD 617 g
617 g
Method B; ASTM D1922
Elmendorf Tear Strength, MD 9.06 g/micron
230 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 30.364 g/micron
771.25 g/mil
ASTM D1922
Dart Drop Test <= 100 g
<= 0.221 lb
Method B; ASTM D1709
130 g
0.287 lb
Method A; ASTM D1709
Film Tensile Strength at Break, MD 49.79 MPa
7221 psi
ASTM D882
Film Tensile Strength at Break, TD 36.10 MPa
5236 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Dow Method (DSC)
Vicat Softening Point 99.0 °C
210 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
ASTM D1003
Gloss 95 %
95 %
45°; ASTM D2457
156 %
156 %
20°; ASTM D2457
Descriptive Properties Value Comments
Cling g 214
ASTM D5458, unstretched