Dow TUFLIN™ HSE-7002 NT 7 Linear Low Density Polyethylene Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Dow Chemical
Trade Name	TUFLIN™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow TUFLIN™ HSE-7002 NT 7 Linear Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Industrial pallet wrap stretch film applications Premium film packaging applications Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a TUFLIN™ HSE-7002 NT 7 is an ethylene-hexene-1 copolymer, designed for cast stretch film applications such as industrial pallet wrap. Films containing HSE-7002 offer outstanding puncture, toughness and load holding properties.Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.9178 g/cc	0.03316 lb/in³	ASTM D792
Thickness	20.3 microns	0.800 mil
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	10.60 MPa	1538 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.29 MPa	1638 psi	ASTM D882
Film Elongation at Break, MD	481 %	481 %	ASTM D882
Film Elongation at Break, TD	891 %	891 %	ASTM D882
Elongation at Break	295 %	295 %	on-pallet testing: Ultimate Stretch; Highlight Industries Method
Secant Modulus, MD	0.1422 GPa	20.63 ksi	2% Secant; ASTM D882
Secant Modulus, TD	0.1504 GPa	21.82 ksi	2% Secant; ASTM D882
Impact	10	10	[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
	372	372	[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
	2453	2453	[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
	4321	4321	[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Puncture Energy	4.29 J	3.17 ft-lb	Dow Method
Elmendorf Tear Strength MD	224 g	224 g	Method B; ASTM D1922
Elmendorf Tear Strength TD	640 g	640 g	Method B; ASTM D1922
Elmendorf Tear Strength, MD	11.0 g/micron	280 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	31.5 g/micron	800 g/mil	ASTM D1922
Dart Drop Test	<= 100 g	<= 0.221 lb	Method B; ASTM D1709
	134 g	0.295 lb	Method A; ASTM D1709
Film Tensile Strength at Break, MD	55.66 MPa	8073 psi	ASTM D882
Film Tensile Strength at Break, TD	47.22 MPa	6849 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	123 °C	253 °F	Dow Method (DSC)
Vicat Softening Point	99.0 °C	210 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	1.0 %	1.0 %	ASTM D1003
Gloss	95 %	95 %	45°; ASTM D2457
	157 %	157 %	20°; ASTM D2457

Descriptive Properties	Value	Comments
Cling g	218	ASTM D5458, unstretched