DuPont™ Kapton® 120FN616 Polyimide/FEP Composite Film
| Category | Polymer , Film , Thermoset , Polyimide, TS , Polyimide, Thermoset Film |
| Manufacturer | DuPont |
| Trade Name | Kapton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont™ Kapton® 120FN616 Polyimide/FEP Composite Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
120 Gauge film structure consisting of a 25 µm (1 mil) base polyimide film with a 2.5 µm (0.1 mil) coating of Teflon® FEP on both sides.Kapton® Type HN film coated with Teflon® FEP fluoropolymer resin, imparts heat sealability, provides a moisture barrier, and enhances chemical resistance.General Kapton® information: Kapton® is synthesized by polymerizing an aromatic dianhydride with an aromatic diamine. It has excellent chemical resistance; there are no known organic solvents for the film. It does not melt. It can be used at both high and low temperature extremes. Kapton® polyimide films can be used in a variety of electrical and electronic uses: wire and cable tapes, formed coil insulation, substrates for printed circuit boards, motor slot liners, magnet wire insulation, transformer and capacitor insulation, magnetic and pressure-sensitive tapes, and tubing.Data provided by DuPont High Performance Films.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D542-90 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 50% RH; 23°C |
| Water Absorption at Saturation | 2.5 % | 2.5 % | 98% RH; 23°C |
| Water Vapor Transmission | 17.5 g/m²/day | 1.13 g/100 in²/day |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 42.0 MPa @Temperature 200 °C |
6090 psi @Temperature 392 °F |
3% yield point. Orientation not specified; ASTM D882-91 |
| 61.0 MPa @Temperature 23.0 °C |
8850 psi @Temperature 73.4 °F |
3% yield point. Orientation not specified; ASTM D882-91 | |
| Film Elongation at Break, MD | 75 % | 75 % | Orientation not specified. Value at 200°C (390°F) is 80%; ASTM D882 |
| Secant Modulus | 1.62 GPa @Temperature 200 °C |
235 ksi @Temperature 392 °F |
ASTM D882 |
| 2.48 GPa @Temperature 23.0 °C |
360 ksi @Temperature 73.4 °F |
ASTM D882 | |
| Impact Test | 0.780 J | 0.575 ft-lb | Impact strength per DuPont Pneumatic Impact Test |
| Tear Strength Test | 11.8 | 11.8 | N Graves (Initial) value; ASTM D1004-90 |
| Elmendorf Tear Strength MD | 8.2 g | 8.2 g | Orientation not specified; ASTM D1922-89 |
| Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | Orientation not specified; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.09 J/g-°C | 0.261 BTU/lb-°F | Value for Kapton® HN |
| Thermal Conductivity | 0.120 W/m-K | 0.833 BTU-in/hr-ft²-°F | Value for Kapton® HN |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.40e+17 ohm-cm | 1.40e+17 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 272 kV/mm | 6910 kV/in | |
| Dissipation Factor | 0.0015 | 0.0015 |