DuPont Performance Polymers Crastin® HR5330HFS NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® HR5330HFS NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Polybutylene Terephthalate with Improved Processing Crastin HR5330HFS is a 30% glass fiber reinforced moderately toughened hydrolysis resistant polybutylene terephthalate for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 0.35 %

@Thickness 2.00 mm
 0.35 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %

@Thickness 2.00 mm
 0.150 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 230000 cP

@Temperature 250 °C
 230000 cP

@Temperature 482 °F
 @ 1000 sec-1; ISO 11443
68400 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
 68400 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
81500 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 81500 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
98700 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 98700 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
211600 cP

@Shear Rate 500 1/s,
Temperature 270 °C
 211600 cP

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
253100 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 253100 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
300300 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 300300 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4 2577
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 7.5 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527-1/-2
Tensile Stress 8.01 MPa

@Strain 0.240 %,
Temperature 150 °C
 1160 psi

@Strain 0.240 %,
Temperature 302 °F
 ISO 11403-1 -2
10.04 MPa

@Strain 0.210 %,
Temperature 90.0 °C
 1456 psi

@Strain 0.210 %,
Temperature 194 °F
 ISO 11403-1 -2
23.3 MPa

@Strain 0.330 %,
Temperature 40.0 °C
 3380 psi

@Strain 0.330 %,
Temperature 104 °F
 ISO 11403-1 -2
26.61 MPa

@Strain 1.05 %,
Temperature 150 °C
 3859 psi

@Strain 1.05 %,
Temperature 302 °F
 ISO 11403-1 -2
32.96 MPa

@Strain 0.360 %,
Temperature 23.0 °C
 4780 psi

@Strain 0.360 %,
Temperature 73.4 °F
 ISO 11403-1 -2
33.14 MPa

@Strain 0.830 %,
Temperature 90.0 °C
 4807 psi

@Strain 0.830 %,
Temperature 194 °F
 ISO 11403-1 -2
37.33 MPa

@Strain 1.98 %,
Temperature 150 °C
 5414 psi

@Strain 1.98 %,
Temperature 302 °F
 ISO 11403-1 -2
43.6 MPa

@Strain 2.96 %,
Temperature 150 °C
 6320 psi

@Strain 2.96 %,
Temperature 302 °F
 ISO 11403-1 -2
43.81 MPa

@Strain 0.440 %,
Temperature 0.000 °C
 6354 psi

@Strain 0.440 %,
Temperature 32.0 °F
 ISO 11403-1 -2
49.22 MPa

@Strain 1.53 %,
Temperature 90.0 °C
 7139 psi

@Strain 1.53 %,
Temperature 194 °F
 ISO 11403-1 -2
57.24 MPa

@Strain 0.960 %,
Temperature 40.0 °C
 8302 psi

@Strain 0.960 %,
Temperature 104 °F
 ISO 11403-1 -2
59.41 MPa

@Strain 2.26 %,
Temperature 90.0 °C
 8617 psi

@Strain 2.26 %,
Temperature 194 °F
 ISO 11403-1 -2
65.44 MPa

@Strain 0.660 %,
Temperature -20.0 °C
 9491 psi

@Strain 0.660 %,
Temperature -4.00 °F
 ISO 11403-1 -2
66.81 MPa

@Strain 0.790 %,
Temperature 23.0 °C
 9690 psi

@Strain 0.790 %,
Temperature 73.4 °F
 ISO 11403-1 -2
74.56 MPa

@Strain 0.790 %,
Temperature 0.000 °C
 10810 psi

@Strain 0.790 %,
Temperature 32.0 °F
 ISO 11403-1 -2
76.98 MPa

@Strain 1.51 %,
Temperature 40.0 °C
 11170 psi

@Strain 1.51 %,
Temperature 104 °F
 ISO 11403-1 -2
84.73 MPa

@Strain 0.790 %,
Temperature -40.0 °C
 12290 psi

@Strain 0.790 %,
Temperature -40.0 °F
 ISO 11403-1 -2
91.45 MPa

@Strain 1.21 %,
Temperature 23.0 °C
 13260 psi

@Strain 1.21 %,
Temperature 73.4 °F
 ISO 11403-1 -2
91.85 MPa

@Strain 2.14 %,
Temperature 40.0 °C
 13320 psi

@Strain 2.14 %,
Temperature 104 °F
 ISO 11403-1 -2
103.45 MPa

@Strain 1.19 %,
Temperature 0.000 °C
 15004 psi

@Strain 1.19 %,
Temperature 32.0 °F
 ISO 11403-1 -2
110.95 MPa

@Strain 1.68 %,
Temperature 23.0 °C
 16092 psi

@Strain 1.68 %,
Temperature 73.4 °F
 ISO 11403-1 -2
121.04 MPa

@Strain 1.33 %,
Temperature -20.0 °C
 17555 psi

@Strain 1.33 %,
Temperature -4.00 °F
 ISO 11403-1 -2
122.73 MPa

@Strain 1.21 %,
Temperature -40.0 °C
 17801 psi

@Strain 1.21 %,
Temperature -40.0 °F
 ISO 11403-1 -2
128.42 MPa

@Strain 1.66 %,
Temperature 0.000 °C
 18626 psi

@Strain 1.66 %,
Temperature 32.0 °F
 ISO 11403-1 -2
159.43 MPa

@Strain 2.06 %,
Temperature -20.0 °C
 23123 psi

@Strain 2.06 %,
Temperature -4.00 °F
 ISO 11403-1 -2
168.02 MPa

@Strain 1.85 %,
Temperature -40.0 °C
 24369 psi

@Strain 1.85 %,
Temperature -40.0 °F
 ISO 11403-1 -2
198.29 MPa

@Strain 2.50 %,
Temperature -40.0 °C
 28760 psi

@Strain 2.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 3.1 %
3.1 %
ISO 527-1/-2
Tensile Modulus 8.50 GPa
1230 ksi
ISO 527-1/-2
Flexural Strength 195 MPa
28300 psi
ISO 178
Secant Modulus 3.76 GPa

@Strain 2.64 %,
Temperature 40.0 °C
 545 ksi

@Strain 2.64 %,
Temperature 104 °F
 ISO 11403-1 -2
4.83 GPa

@Strain 1.71 %,
Temperature 40.0 °C
 701 ksi

@Strain 1.71 %,
Temperature 104 °F
 ISO 11403-1 -2
5.91 GPa

@Strain 2.05 %,
Temperature 23.0 °C
 857 ksi

@Strain 2.05 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.9625 GPa

@Strain 0.960 %,
Temperature 40.0 °C
 864.80 ksi

@Strain 0.960 %,
Temperature 104 °F
 ISO 11403-1 -2
6.98 GPa

@Strain 2.05 %,
Temperature 0.000 °C
 1010 ksi

@Strain 2.05 %,
Temperature 32.0 °F
 ISO 11403-1 -2
7.06 GPa

@Strain 0.330 %,
Temperature 40.0 °C
 1020 ksi

@Strain 0.330 %,
Temperature 104 °F
 ISO 11403-1 -2
7.25 GPa

@Strain 1.36 %,
Temperature 23.0 °C
 1050 ksi

@Strain 1.36 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.33 GPa

@Strain 2.30 %,
Temperature -20.0 °C
 1060 ksi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.40 GPa

@Strain 1.34 %,
Temperature 0.000 °C
 1220 ksi

@Strain 1.34 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.46 GPa

@Strain 0.790 %,
Temperature 23.0 °C
 1230 ksi

@Strain 0.790 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.68 GPa

@Strain 2.06 %,
Temperature -40.0 °C
 1260 ksi

@Strain 2.06 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.10 GPa

@Strain 1.33 %,
Temperature -20.0 °C
 1320 ksi

@Strain 1.33 %,
Temperature -4.00 °F
 ISO 11403-1 -2
9.16 GPa

@Strain 0.360 %,
Temperature 23.0 °C
 1330 ksi

@Strain 0.360 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.44 GPa

@Strain 0.790 %,
Temperature 0.000 °C
 1370 ksi

@Strain 0.790 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.92 GPa

@Strain 0.660 %,
Temperature -20.0 °C
 1440 ksi

@Strain 0.660 %,
Temperature -4.00 °F
 ISO 11403-1 -2
9.96 GPa

@Strain 0.440 %,
Temperature 0.000 °C
 1440 ksi

@Strain 0.440 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.143 GPa

@Strain 1.21 %,
Temperature -40.0 °C
 1471.1 ksi

@Strain 1.21 %,
Temperature -40.0 °F
 ISO 11403-1 -2
10.7 GPa

@Strain 0.790 %,
Temperature -40.0 °C
 1560 ksi

@Strain 0.790 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179/1eA
1.00 J/cm²

@Temperature -40.0 °C
 4.76 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA