DuPont Performance Polymers Crastin® LW9330 NC010 PBT+SAN  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® LW9330 NC010 PBT+SAN  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9330 NC010 is a 30% glass fiber reinforced polybutylene terephthalate blend for injection molding. It has improved surface aesthetics excellent dimensionalInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.0 %

@Thickness 2.00 mm
 1.0 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.250 %

@Thickness 2.00 mm
 0.250 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 72620 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 72620 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
80869 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 80869 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
90740 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 90740 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
318500 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 318500 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
369400 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 369400 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
428400 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 428400 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
ISO 527-1/-2
Tensile Stress 3.97 MPa

@Strain 0.250 %,
Temperature 150 °C
 576 psi

@Strain 0.250 %,
Temperature 302 °F
 ISO 11403-1 -2
8.22 MPa

@Strain 0.150 %,
Temperature 90.0 °C
 1190 psi

@Strain 0.150 %,
Temperature 194 °F
 ISO 11403-1 -2
15.28 MPa

@Strain 1.77 %,
Temperature 150 °C
 2216 psi

@Strain 1.77 %,
Temperature 302 °F
 ISO 11403-1 -2
17.5 MPa

@Strain 2.53 %,
Temperature 150 °C
 2540 psi

@Strain 2.53 %,
Temperature 302 °F
 ISO 11403-1 -2
19.01 MPa

@Strain 3.28 %,
Temperature 150 °C
 2757 psi

@Strain 3.28 %,
Temperature 302 °F
 ISO 11403-1 -2
21.56 MPa

@Strain 5.55 %,
Temperature 150 °C
 3127 psi

@Strain 5.55 %,
Temperature 302 °F
 ISO 11403-1 -2
24.51 MPa

@Strain 0.320 %,
Temperature 40.0 °C
 3555 psi

@Strain 0.320 %,
Temperature 104 °F
 ISO 11403-1 -2
28.64 MPa

@Strain 0.280 %,
Temperature -20.0 °C
 4154 psi

@Strain 0.280 %,
Temperature -4.00 °F
 ISO 11403-1 -2
33.29 MPa

@Strain 0.350 %,
Temperature 0.000 °C
 4828 psi

@Strain 0.350 %,
Temperature 32.0 °F
 ISO 11403-1 -2
48.94 MPa

@Strain 1.34 %,
Temperature 90.0 °C
 7098 psi

@Strain 1.34 %,
Temperature 194 °F
 ISO 11403-1 -2
55.89 MPa

@Strain 1.93 %,
Temperature 90.0 °C
 8106 psi

@Strain 1.93 %,
Temperature 194 °F
 ISO 11403-1 -2
58.68 MPa

@Strain 2.37 %,
Temperature 90.0 °C
 8511 psi

@Strain 2.37 %,
Temperature 194 °F
 ISO 11403-1 -2
64.56 MPa

@Strain 0.940 %,
Temperature 40.0 °C
 9364 psi

@Strain 0.940 %,
Temperature 104 °F
 ISO 11403-1 -2
72.75 MPa

@Strain 0.840 %,
Temperature 23.0 °C
 10550 psi

@Strain 0.840 %,
Temperature 73.4 °F
 ISO 11403-1 -2
78.69 MPa

@Strain 1.25 %,
Temperature 40.0 °C
 11410 psi

@Strain 1.25 %,
Temperature 104 °F
 ISO 11403-1 -2
89.84 MPa

@Strain 1.56 %,
Temperature 40.0 °C
 13030 psi

@Strain 1.56 %,
Temperature 104 °F
 ISO 11403-1 -2
101.03 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 14653 psi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
105.92 MPa

@Strain 2.50 %,
Temperature 40.0 °C
 15362 psi

@Strain 2.50 %,
Temperature 104 °F
 ISO 11403-1 -2
107.31 MPa

@Strain 1.20 %,
Temperature -20.0 °C
 15564 psi

@Strain 1.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
110.09 MPa

@Strain 1.33 %,
Temperature 0.000 °C
 15967 psi

@Strain 1.33 %,
Temperature 32.0 °F
 ISO 11403-1 -2
119.01 MPa

@Strain 1.75 %,
Temperature 23.0 °C
 17261 psi

@Strain 1.75 %,
Temperature 73.4 °F
 ISO 11403-1 -2
124.94 MPa

@Strain 1.59 %,
Temperature 0.000 °C
 18121 psi

@Strain 1.59 %,
Temperature 32.0 °F
 ISO 11403-1 -2
125.12 MPa

@Strain 1.47 %,
Temperature -20.0 °C
 18147 psi

@Strain 1.47 %,
Temperature -4.00 °F
 ISO 11403-1 -2
125.56 MPa

@Strain 2.03 %,
Temperature 23.0 °C
 18211 psi

@Strain 2.03 %,
Temperature 73.4 °F
 ISO 11403-1 -2
139.24 MPa

@Strain 1.94 %,
Temperature 0.000 °C
 20195 psi

@Strain 1.94 %,
Temperature 32.0 °F
 ISO 11403-1 -2
153.56 MPa

@Strain 2.03 %,
Temperature -20.0 °C
 22272 psi

@Strain 2.03 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 2.3 %
2.3 %
ISO 527-1/-2
Tensile Modulus 9.80 GPa
1420 ksi
ISO 527-1/-2
1.527 GPa

@Temperature 150 °C
 221.5 ksi

@Temperature 302 °F
 ISO 11403-1 -2
6.458 GPa

@Temperature 60.0 °C
 936.7 ksi

@Temperature 140 °F
 ISO 11403-1 -2
10.439 GPa

@Temperature -20.0 °C
 1514.1 ksi

@Temperature -4.00 °F
 ISO 11403-1 -2
Flexural Modulus 8.40 GPa
1220 ksi
ISO 178
Secant Modulus 4.71 GPa

@Strain 2.19 %,
Temperature 40.0 °C
 683 ksi

@Strain 2.19 %,
Temperature 104 °F
 ISO 11403-1 -2
5.39 GPa

@Strain 1.77 %,
Temperature 40.0 °C
 782 ksi

@Strain 1.77 %,
Temperature 104 °F
 ISO 11403-1 -2
5.61 GPa

@Strain 2.30 %,
Temperature 23.0 °C
 814 ksi

@Strain 2.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.10 GPa

@Strain 1.36 %,
Temperature 40.0 °C
 884 ksi

@Strain 1.36 %,
Temperature 104 °F
 ISO 11403-1 -2
6.60 GPa

@Strain 1.84 %,
Temperature 23.0 °C
 957 ksi

@Strain 1.84 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.85 GPa

@Strain 2.11 %,
Temperature 0.000 °C
 993 ksi

@Strain 2.11 %,
Temperature 32.0 °F
 ISO 11403-1 -2
6.87 GPa

@Strain 0.940 %,
Temperature 40.0 °C
 996 ksi

@Strain 0.940 %,
Temperature 104 °F
 ISO 11403-1 -2
7.03 GPa

@Strain 2.30 %,
Temperature -20.0 °C
 1020 ksi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
7.50 GPa

@Strain 1.77 %,
Temperature 0.000 °C
 1090 ksi

@Strain 1.77 %,
Temperature 32.0 °F
 ISO 11403-1 -2
7.66 GPa

@Strain 0.320 %,
Temperature 40.0 °C
 1110 ksi

@Strain 0.320 %,
Temperature 104 °F
 ISO 11403-1 -2
7.77 GPa

@Strain 1.30 %,
Temperature 23.0 °C
 1130 ksi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.90 GPa

@Strain 1.85 %,
Temperature -20.0 °C
 1150 ksi

@Strain 1.85 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.28 GPa

@Strain 1.33 %,
Temperature 0.000 °C
 1200 ksi

@Strain 1.33 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.66 GPa

@Strain 0.840 %,
Temperature 23.0 °C
 1260 ksi

@Strain 0.840 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.9425 GPa

@Strain 1.20 %,
Temperature -20.0 °C
 1297.0 ksi

@Strain 1.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
9.51 GPa

@Strain 0.350 %,
Temperature 0.000 °C
 1380 ksi

@Strain 0.350 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.2 GPa

@Strain 0.280 %,
Temperature -20.0 °C
 1480 ksi

@Strain 0.280 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
7.00 kJ/m²

@Temperature -40.0 °C
 3.33 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
ISO 180/1U