DuPont Performance Polymers Crastin® S600F10 BK851 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® S600F10 BK851 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® S600F10 BK851 is an unreinforced, lubricated, medium high viscosity, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength, Yield 57.0 MPa

@Temperature 23.0 °C
 8270 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break >= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 nominal; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
 377 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 85.0 MPa

@Temperature 23.0 °C
 12300 psi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ISO 75-1/-2
180 °C
356 °F
Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Annealed; ISO 75-1/-2
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746B
130 °C

@Thickness 6.00 mm
 266 °F

@Thickness 0.236 in
 UL 746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746B
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746B
115 °C

@Thickness 6.00 mm
 239 °F

@Thickness 0.236 in
 UL 746B
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical without Impact 120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
 UL 746B
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746B
120 °C

@Thickness 6.00 mm
 248 °F

@Thickness 0.236 in
 UL 746B
120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
 UL 746B
Flammability, UL94 HB

@Thickness 6.00 mm
 HB

@Thickness 0.236 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 UL94
HB

@Thickness 6.00 mm
 HB

@Thickness 0.236 in
 UL94
Oxygen Index 21 %
21 %
ISO 4589-1/-2
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Optimum
240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
optimum
30.0 - 130 °C
86.0 - 266 °F
Drying Temperature 110 - 130 °C
230 - 266 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.040 %
<= 0.040 %
Descriptive Properties Value Comments
Additive Lubricant
Appearance Black Color
Drying Recommended Yes
Features Chemical Resistance, Good
Dimensional Stability, Good
Lubricated
Moisture Absorption, Low
Processability, Good
Viscosity, High
Viscosity, Medium-High
Forms Pellets
Generic PBT
Material Status Current
Part Marking Code >PBT<
ISO 11469
Processing Method Injection Molding
Product Category Unreinforced Resins
Region Available - Global Yes
Resin Identification PBT
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Automotive Applications
Electrical Parts
Electrical/Electronic Applications
Parts, Engineering
Parts, Industrial
Parts, Machine/Mechanical
Parts, Thick-walled