DuPont Performance Polymers Crastin® ST830FRUV NC010 PBT (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Crastin® ST830FRUV NC010 PBT (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Crastin® ST830FRUV NC010 is an unreinforced, Super Tough, flame retardant polybutylene terephthalate resin for injection molding. It contains a UV light stabilizer and is recognized as UL94V-0 at 0.85mm (0.033in).Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.016 cm/cm @Thickness 2.00 mm	0.016 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	40.0 MPa @Temperature 23.0 °C	5800 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	45 % @Temperature 23.0 °C	45 % @Temperature 73.4 °F	nominal; ISO 527
Elongation at Yield	9.0 % @Temperature 23.0 °C	9.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.20 GPa @Temperature 23.0 °C	319 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/m² @Temperature -40.0 °C	4.76 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
	10.0 kJ/m² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	70.0 kJ/m² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Izod Impact, Unnotched (ISO)	220 kJ/m² @Temperature -40.0 °C	105 ft-lb/in² @Temperature -40.0 °F	ISO 180/1U
	220 kJ/m² @Temperature -30.0 °C	105 ft-lb/in² @Temperature -22.0 °F	ISO 180/1U
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	35.0 J/cm² @Temperature -40.0 °C	167 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eU
	35.0 J/cm² @Temperature -30.0 °C	167 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm² @Temperature -40.0 °C	4.76 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eA
	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	6.50 J/cm² @Temperature 23.0 °C	30.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	125 °C	257 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-1/-2
UL RTI, Electrical	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
	130 °C @Thickness 0.850 mm	266 °F @Thickness 0.0335 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
UL RTI, Mechanical with Impact	130 °C @Thickness 0.850 mm	266 °F @Thickness 0.0335 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical without Impact	130 °C @Thickness 0.850 mm	266 °F @Thickness 0.0335 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
Flammability, UL94	V-0 @Thickness 0.850 mm	V-0 @Thickness 0.0335 in	IEC 60695-11-10
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
	V-0 @Thickness 0.850 mm	V-0 @Thickness 0.0335 in	UL94
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL94
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	UL94

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	>= 600 V @Temperature 23.0 °C	>= 600 V @Temperature 73.4 °F	UL 746A

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Optimum
	240 - 260 °C	464 - 500 °F
Mold Temperature	80.0 °C	176 °F	optimum
	30.0 - 130 °C	86.0 - 266 °F
Drying Temperature	110 - 130 °C	230 - 266 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	<= 0.040 %	<= 0.040 %

Descriptive Properties	Value	Comments
Additive	Impact Modifier
	Lubricant
	UV Stabilizer
Appearance	Natural Color
Drying Recommended	Yes
Features	Chemical Resistance, Good
	Dimensional Stability, Good
	Flame Retardant
	Impact Resistance, High
	Moisture Absorption, Low
	Processability, Good
	UV Resistance, Good
Forms	Pellets
Generic	PBT
Material Status	Current
Part Marking Code	>PBT-HIFR(17)<	ISO 11469
Processing Method	Injection Molding
Product Category	Extrusion Resins
	Flame Retardant Resins
	Toughened Resins
	UV Resistant/Weatherable Resins
Resin Identification	PBT-HIFR(17)	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Connectors
	Electrical/Electronic Applications