DuPont Performance Polymers Delrin® 100AF Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 100AF Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

20% Teflon® Fiber Filled High Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 100AF is a high viscosity acetal homopolymer containing 20% Teflon PTFE fibers. It is designed for applications requiring low wear and/or low friction agaiInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.54 g/cc	0.0556 lb/in³	ISO 1183
Viscosity	111000 cP @Shear Rate 5000 1/s, Temperature 230 °C	111000 cP @Shear Rate 5000 1/s, Temperature 446 °F	ISO 11403-1 -2
	128000 cP @Shear Rate 5000 1/s, Temperature 215 °C	128000 cP @Shear Rate 5000 1/s, Temperature 419 °F	ISO 11403-1 -2
	151000 cP @Shear Rate 5000 1/s, Temperature 200 °C	151000 cP @Shear Rate 5000 1/s, Temperature 392 °F	ISO 11403-1 -2
	441000 cP @Shear Rate 500 1/s, Temperature 230 °C	441000 cP @Shear Rate 500 1/s, Temperature 446 °F	ISO 11403-1 -2
	509000 cP @Shear Rate 500 1/s, Temperature 215 °C	509000 cP @Shear Rate 500 1/s, Temperature 419 °F	ISO 11403-1 -2
	598000 cP @Shear Rate 500 1/s, Temperature 200 °C	598000 cP @Shear Rate 500 1/s, Temperature 392 °F	ISO 11403-1 -2
Linear Mold Shrinkage, Flow	0.021 cm/cm	0.021 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	ISO 294-4 2577
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 °C	1.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	53.0 MPa	7690 psi	ISO 527-1/-2
Elongation at Break	15 %	15 %	ISO 527-1/-2
Tensile Modulus	2.70 GPa	392 ksi	ISO 527-1/-2
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 µm/m-°C	61.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	110 µm/m-°C	61.1 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	87.0 °C	189 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10

Descriptive Properties	Value	Comments
Additives	Lubricants
	Release agent
Delivery Form	Pellets
Part Marking Code	>POM-SF20<	ISO 11469
Processing	Injection Moulding
	Other Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-SF20	ISO 1043
UL recognition	UL