DuPont Performance Polymers Delrin® 100AL NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100AL NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lubricated High Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 100AL NC010 an unreinforced high viscosity lubricated acetal homopolymer resin containing an advanced system of lubrication for low wear and friction against metals andInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Viscosity 111000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 111000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
129000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 129000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
152000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 152000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
432000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 432000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
502000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 502000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
593000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 593000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 44.9 MPa

@Strain 2.20 %,
Temperature 23.0 °C
 6510 psi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
57.6 MPa

@Strain 1.80 %,
Temperature -40.0 °C
 8350 psi

@Strain 1.80 %,
Temperature -40.0 °F
 ISO 11403-1 -2
64.5 MPa

@Strain 8.00 %,
Temperature 23.0 °C
 9350 psi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.6 MPa

@Strain 15.0 %,
Temperature 23.0 °C
 9510 psi

@Strain 15.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
94.1 MPa

@Strain 7.00 %,
Temperature -40.0 °C
 13600 psi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
96.0 MPa

@Strain 13.0 %,
Temperature -40.0 °C
 13900 psi

@Strain 13.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 45 %
45 %
Nominal; ISO 527-1/-2
Elongation at Yield 18 %
18 %
ISO 527-1/-2
Tensile Modulus 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Secant Modulus 0.141 GPa

@Strain 19.0 %,
Temperature 100 °C
 20.4 ksi

@Strain 19.0 %,
Temperature 212 °F
 ISO 11403-1 -2
0.192 GPa

@Strain 19.0 %,
Temperature 80.0 °C
 27.8 ksi

@Strain 19.0 %,
Temperature 176 °F
 ISO 11403-1 -2
0.286 GPa

@Strain 9.00 %,
Temperature 100 °C
 41.4 ksi

@Strain 9.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.386 GPa

@Strain 17.0 %,
Temperature 23.0 °C
 56.1 ksi

@Strain 17.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.393 GPa

@Strain 9.00 %,
Temperature 80.0 °C
 57.0 ksi

@Strain 9.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.640 GPa

@Strain 15.0 %,
Temperature -40.0 °C
 92.8 ksi

@Strain 15.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.80625 GPa

@Strain 8.00 %,
Temperature 23.0 °C
 116.94 ksi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.854 GPa

@Strain 2.40 %,
Temperature 100 °C
 124 ksi

@Strain 2.40 %,
Temperature 212 °F
 ISO 11403-1 -2
1.14 GPa

@Strain 2.40 %,
Temperature 80.0 °C
 166 ksi

@Strain 2.40 %,
Temperature 176 °F
 ISO 11403-1 -2
1.34 GPa

@Strain 7.00 %,
Temperature -40.0 °C
 195 ksi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.04 GPa

@Strain 2.20 %,
Temperature 23.0 °C
 296 ksi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.20 GPa

@Strain 1.80 %,
Temperature -40.0 °C
 464 ksi

@Strain 1.80 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 25.0 J/cm²
119 ft-lb/in²
ISO 179/1eU
17.0 J/cm²

@Temperature -30.0 °C
 80.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Emissions <8 mg/kg
VDA 275
Part Marking Code >POM-S<
ISO 11469
Processing Injection Moulding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-S
ISO 1043
UL recognition UL