DuPont Performance Polymers Delrin® 150 NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 150 NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has excellent thermal stability, low die deposit, and enhanced crystallization for low porosity.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.39 %

@Temperature 23.0 °C
0.39 %

@Temperature 73.4 °F
Immersion 24h; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 2.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Melt Index of Compound 1.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 72.0 MPa

@Temperature 23.0 °C
10400 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 40 %

@Temperature 23.0 °C
40 %

@Temperature 73.4 °F
nominal; ISO 527
Elongation at Yield 22 %

@Temperature 23.0 °C
22 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.10 GPa

@Temperature 23.0 °C
450 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 2.90 GPa

@Temperature 23.0 °C
421 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
278 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
100 µm/m-°C

@Temperature 23.0 - 55.0 °C
55.6 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
150 µm/m-°C

@Temperature 55.0 - 100 °C
83.3 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
UL RTI, Electrical 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
UL 746B
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
UL 746B
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
UL 746B
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
Electrical Properties Metric English Comments
Dissipation Factor 0.0060

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.0060

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Processing Properties Metric English Comments
Melt Temperature 200 °C
392 °F
Optimum; Extrusion
195 - 205 °C
383 - 401 °F
Extrusion
210 - 220 °C
410 - 428 °F
Injection Molding
215 °C
419 °F
Optimum; Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.20 %
<= 0.20 %
Extrusion
<= 0.20 %
<= 0.20 %
Injection Molding
Descriptive Properties Value Comments
Appearance Natural Color
Extrudable - Cast Film Yes
Extrudable - Sheet Yes
Extrudable - Tubing Yes
Extrudable - Wire and Cable Yes
Features Creep Resistance, Good
Dimensional Stability, Good
Fatigue Resistant
Homopolymer
Impact Resistance, High
Molecular Wt., High
Stiffness, High
Strength, High
Toughness, Good
Viscosity, High
Forms Pellets
Generic Acetal (POM) Homopolymer
Material Status Current
Part Marking Code >POM<
ISO 11469
Polymer Family POM
Polymer Type POM Homopolymer
Processing Method Extrusion
Product Category Extrusion Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification POM
ISO 1043
RoHS Compliance Contact Manufacturer
Ultrasonic Weldable Yes
Uses Parts, Engineering