DuPont Performance Polymers Delrin® 500CL NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500CL NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500CL is a medium viscosity acetal homopolymer resin containing a chemical lubricant designed for low wear and friction against metals.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 1.0 %

@Thickness 2.00 mm
 1.0 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.250 %

@Thickness 2.00 mm
 0.250 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 9.90 MPa

@Strain 1.10 %,
Temperature 90.0 °C
 1440 psi

@Strain 1.10 %,
Temperature 194 °F
 ISO 11403-1 -2
25.6 MPa

@Strain 4.60 %,
Temperature 90.0 °C
 3710 psi

@Strain 4.60 %,
Temperature 194 °F
 ISO 11403-1 -2
27.5 MPa

@Strain 1.40 %,
Temperature 40.0 °C
 3990 psi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
28.9 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 4190 psi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
31.4 MPa

@Strain 8.00 %,
Temperature 90.0 °C
 4550 psi

@Strain 8.00 %,
Temperature 194 °F
 ISO 11403-1 -2
32.6 MPa

@Strain 11.4 %,
Temperature 90.0 °C
 4730 psi

@Strain 11.4 %,
Temperature 194 °F
 ISO 11403-1 -2
41.8 MPa

@Strain 1.50 %,
Temperature 0.000 °C
 6060 psi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
45.7 MPa

@Strain 1.40 %,
Temperature -20.0 °C
 6630 psi

@Strain 1.40 %,
Temperature -4.00 °F
 ISO 11403-1 -2
52.3 MPa

@Strain 1.60 %,
Temperature -40.0 °C
 7590 psi

@Strain 1.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
52.9 MPa

@Strain 5.50 %,
Temperature 40.0 °C
 7670 psi

@Strain 5.50 %,
Temperature 104 °F
 ISO 11403-1 -2
57.1 MPa

@Strain 9.60 %,
Temperature 40.0 °C
 8280 psi

@Strain 9.60 %,
Temperature 104 °F
 ISO 11403-1 -2
58.0 MPa

@Strain 4.40 %,
Temperature 23.0 °C
 8410 psi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
63.8 MPa

@Strain 7.60 %,
Temperature 23.0 °C
 9250 psi

@Strain 7.60 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.0 MPa

@Strain 10.9 %,
Temperature 23.0 °C
 9430 psi

@Strain 10.9 %,
Temperature 73.4 °F
 ISO 11403-1 -2
70.9 MPa

@Strain 5.80 %,
Temperature 0.000 °C
 10300 psi

@Strain 5.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
73.6 MPa

@Strain 10.2 %,
Temperature 0.000 °C
 10700 psi

@Strain 10.2 %,
Temperature 32.0 °F
 ISO 11403-1 -2
74.1 MPa

@Strain 14.6 %,
Temperature 0.000 °C
 10700 psi

@Strain 14.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
78.2 MPa

@Strain 5.50 %,
Temperature -20.0 °C
 11300 psi

@Strain 5.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
81.9 MPa

@Strain 9.70 %,
Temperature -20.0 °C
 11900 psi

@Strain 9.70 %,
Temperature -4.00 °F
 ISO 11403-1 -2
82.2 MPa

@Strain 13.8 %,
Temperature -20.0 °C
 11900 psi

@Strain 13.8 %,
Temperature -4.00 °F
 ISO 11403-1 -2
93.9 MPa

@Strain 6.40 %,
Temperature -40.0 °C
 13600 psi

@Strain 6.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
96.7 MPa

@Strain 11.1 %,
Temperature -40.0 °C
 14000 psi

@Strain 11.1 %,
Temperature -40.0 °F
 ISO 11403-1 -2
97.1 MPa

@Strain 15.9 %,
Temperature -40.0 °C
 14100 psi

@Strain 15.9 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 67.0 MPa
9720 psi
ISO 527-1/-2
Elongation at Break 25 %
25 %
Nominal; ISO 527-1/-2
Elongation at Yield 15 %
15 %
ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-1/-2
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Shear Modulus 0.222 GPa

@Temperature 120 °C
 32.2 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.509 GPa

@Temperature 70.0 °C
 73.8 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.907 GPa

@Temperature 20.0 °C
 132 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.105 GPa

@Temperature -20.0 °C
 160.3 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.29 GPa

@Temperature -50.0 °C
 187 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.308 GPa

@Strain 9.80 %,
Temperature 100 °C
 44.7 ksi

@Strain 9.80 %,
Temperature 212 °F
 ISO 11403-1 -2
0.450 GPa

@Strain 8.60 %,
Temperature 80.0 °C
 65.3 ksi

@Strain 8.60 %,
Temperature 176 °F
 ISO 11403-1 -2
0.498 GPa

@Strain 5.40 %,
Temperature 100 °C
 72.3 ksi

@Strain 5.40 %,
Temperature 212 °F
 ISO 11403-1 -2
0.522 GPa

@Strain 11.0 %,
Temperature 40.0 °C
 75.7 ksi

@Strain 11.0 %,
Temperature 104 °F
 ISO 11403-1 -2
0.632 GPa

@Strain 11.7 %,
Temperature 0.000 °C
 91.7 ksi

@Strain 11.7 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.737 GPa

@Strain 4.30 %,
Temperature 80.0 °C
 107 ksi

@Strain 4.30 %,
Temperature 176 °F
 ISO 11403-1 -2
0.74023 GPa

@Strain 8.70 %,
Temperature 23.0 °C
 107.36 ksi

@Strain 8.70 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.745 GPa

@Strain 11.0 %,
Temperature -20.0 °C
 108 ksi

@Strain 11.0 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.762 GPa

@Strain 12.7 %,
Temperature -40.0 °C
 111 ksi

@Strain 12.7 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.764 GPa

@Strain 2.20 %,
Temperature 100 °C
 111 ksi

@Strain 2.20 %,
Temperature 212 °F
 ISO 11403-1 -2
0.962 GPa

@Strain 5.50 %,
Temperature 40.0 °C
 140 ksi

@Strain 5.50 %,
Temperature 104 °F
 ISO 11403-1 -2
1.22 GPa

@Strain 5.80 %,
Temperature 0.000 °C
 177 ksi

@Strain 5.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.23 GPa

@Strain 1.10 %,
Temperature 80.0 °C
 178 ksi

@Strain 1.10 %,
Temperature 176 °F
 ISO 11403-1 -2
1.32 GPa

@Strain 4.40 %,
Temperature 23.0 °C
 191 ksi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.42 GPa

@Strain 5.50 %,
Temperature -20.0 °C
 206 ksi

@Strain 5.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
1.47 GPa

@Strain 6.40 %,
Temperature -40.0 °C
 213 ksi

@Strain 6.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.96 GPa

@Strain 1.40 %,
Temperature 40.0 °C
 285 ksi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
2.63 GPa

@Strain 1.10 %,
Temperature 23.0 °C
 381 ksi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.79 GPa

@Strain 1.50 %,
Temperature 0.000 °C
 404 ksi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.26 GPa

@Strain 1.40 %,
Temperature -20.0 °C
 473 ksi

@Strain 1.40 %,
Temperature -4.00 °F
 ISO 11403-1 -2
3.27 GPa

@Strain 1.60 %,
Temperature -40.0 °C
 474 ksi

@Strain 1.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
9.00 kJ/m²

@Temperature -40.0 °C
 4.28 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 35.0 J/cm²
167 ft-lb/in²
ISO 179/1eU