DuPont Performance Polymers Delrin® 900P NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 900P NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low Viscosity Acetal Homopolymer with Improved Processing Delrin 900P is a low viscosity acetal homopolymer for injection molding. It has improved processing thermal stability good mechanical properties and low volatile emissions.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.4 %

@Thickness 2.00 mm
1.4 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
0.300 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 73000 cP

@Shear Rate 5000 1/s,
Temperature 235 °C
73000 cP

@Shear Rate 5000 1/s,
Temperature 455 °F
ISO 11403-1 -2
81000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
81000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
ISO 11403-1 -2
89000 cP

@Shear Rate 5000 1/s,
Temperature 195 °C
89000 cP

@Shear Rate 5000 1/s,
Temperature 383 °F
ISO 11403-1 -2
168000 cP

@Shear Rate 500 1/s,
Temperature 235 °C
168000 cP

@Shear Rate 500 1/s,
Temperature 455 °F
ISO 11403-1 -2
214000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
214000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
272000 cP

@Shear Rate 500 1/s,
Temperature 195 °C
272000 cP

@Shear Rate 500 1/s,
Temperature 383 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 190 °C
21 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
25 g/10 min

@Load 2.16 kg,
Temperature 190 °C
25 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 24.6 MPa

@Strain 0.900 %,
Temperature 23.0 °C
3570 psi

@Strain 0.900 %,
Temperature 73.4 °F
ISO 11403-1 -2
25.2 MPa

@Strain 1.20 %,
Temperature 40.0 °C
3650 psi

@Strain 1.20 %,
Temperature 104 °F
ISO 11403-1 -2
27.6 MPa

@Strain 0.800 %,
Temperature 0.000 °C
4000 psi

@Strain 0.800 %,
Temperature 32.0 °F
ISO 11403-1 -2
42.5 MPa

@Strain 1.10 %,
Temperature -40.0 °C
6160 psi

@Strain 1.10 %,
Temperature -40.0 °F
ISO 11403-1 -2
44.6 MPa

@Strain 1.40 %,
Temperature -20.0 °C
6470 psi

@Strain 1.40 %,
Temperature -4.00 °F
ISO 11403-1 -2
53.7 MPa

@Strain 4.70 %,
Temperature 40.0 °C
7790 psi

@Strain 4.70 %,
Temperature 104 °F
ISO 11403-1 -2
58.9 MPa

@Strain 8.20 %,
Temperature 40.0 °C
8540 psi

@Strain 8.20 %,
Temperature 104 °F
ISO 11403-1 -2
61.5 MPa

@Strain 3.50 %,
Temperature 23.0 °C
8920 psi

@Strain 3.50 %,
Temperature 73.4 °F
ISO 11403-1 -2
68.6 MPa

@Strain 3.20 %,
Temperature 0.000 °C
9950 psi

@Strain 3.20 %,
Temperature 32.0 °F
ISO 11403-1 -2
69.9 MPa

@Strain 6.20 %,
Temperature 23.0 °C
10100 psi

@Strain 6.20 %,
Temperature 73.4 °F
ISO 11403-1 -2
78.9 MPa

@Strain 5.60 %,
Temperature 0.000 °C
11400 psi

@Strain 5.60 %,
Temperature 32.0 °F
ISO 11403-1 -2
84.5 MPa

@Strain 5.60 %,
Temperature -20.0 °C
12300 psi

@Strain 5.60 %,
Temperature -4.00 °F
ISO 11403-1 -2
87.0 MPa

@Strain 9.80 %,
Temperature -20.0 °C
12600 psi

@Strain 9.80 %,
Temperature -4.00 °F
ISO 11403-1 -2
93.2 MPa

@Strain 4.40 %,
Temperature -40.0 °C
13500 psi

@Strain 4.40 %,
Temperature -40.0 °F
ISO 11403-1 -2
98.6 MPa

@Strain 7.70 %,
Temperature -40.0 °C
14300 psi

@Strain 7.70 %,
Temperature -40.0 °F
ISO 11403-1 -2
Tensile Strength, Yield 71.0 MPa
10300 psi
ISO 527-1/-2
Elongation at Break 23 %
23 %
Nominal; ISO 527-1/-2
Elongation at Yield 12 %
12 %
ISO 527-1/-2
Tensile Modulus 3.30 GPa
479 ksi
ISO 527-1/-2
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Shear Modulus 0.317 GPa

@Temperature 120 °C
46.0 ksi

@Temperature 248 °F
Dynamic; ISO 11403-1 -2
0.628 GPa

@Temperature 70.0 °C
91.1 ksi

@Temperature 158 °F
Dynamic; ISO 11403-1 -2
1.026 GPa

@Temperature 20.0 °C
148.8 ksi

@Temperature 68.0 °F
Dynamic; ISO 11403-1 -2
1.209 GPa

@Temperature -20.0 °C
175.4 ksi

@Temperature -4.00 °F
Dynamic; ISO 11403-1 -2
1.449 GPa

@Temperature -50.0 °C
210.2 ksi

@Temperature -58.0 °F
Dynamic; ISO 11403-1 -2
Shear Strength 0.0840 MPa

@Shear Rate 500 1/s,
Temperature 235 °C
12.2 psi

@Shear Rate 500 1/s,
Temperature 455 °F
ISO 11403-1 -2
0.107 MPa

@Shear Rate 500 1/s,
Temperature 215 °C
15.5 psi

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
0.136 MPa

@Shear Rate 500 1/s,
Temperature 195 °C
19.7 psi

@Shear Rate 500 1/s,
Temperature 383 °F
ISO 11403-1 -2
Secant Modulus 0.417 GPa

@Strain 7.20 %,
Temperature 100 °C
60.4 ksi

@Strain 7.20 %,
Temperature 212 °F
ISO 11403-1 -2
0.528 GPa

@Strain 7.50 %,
Temperature 80.0 °C
76.6 ksi

@Strain 7.50 %,
Temperature 176 °F
ISO 11403-1 -2
0.629 GPa

@Strain 9.40 %,
Temperature 40.0 °C
91.2 ksi

@Strain 9.40 %,
Temperature 104 °F
ISO 11403-1 -2
0.689 GPa

@Strain 3.60 %,
Temperature 100 °C
99.9 ksi

@Strain 3.60 %,
Temperature 212 °F
ISO 11403-1 -2
0.911 GPa

@Strain 3.70 %,
Temperature 80.0 °C
132 ksi

@Strain 3.70 %,
Temperature 176 °F
ISO 11403-1 -2
1.00 GPa

@Strain 0.900 %,
Temperature 100 °C
145 ksi

@Strain 0.900 %,
Temperature 212 °F
ISO 11403-1 -2
1.01 GPa

@Strain 7.00 %,
Temperature 23.0 °C
146 ksi

@Strain 7.00 %,
Temperature 73.4 °F
ISO 11403-1 -2
1.14 GPa

@Strain 4.70 %,
Temperature 40.0 °C
166 ksi

@Strain 4.70 %,
Temperature 104 °F
ISO 11403-1 -2
1.25 GPa

@Strain 6.40 %,
Temperature 0.000 °C
181 ksi

@Strain 6.40 %,
Temperature 32.0 °F
ISO 11403-1 -2
1.51 GPa

@Strain 5.60 %,
Temperature -20.0 °C
219 ksi

@Strain 5.60 %,
Temperature -4.00 °F
ISO 11403-1 -2
1.53 GPa

@Strain 0.900 %,
Temperature 80.0 °C
222 ksi

@Strain 0.900 %,
Temperature 176 °F
ISO 11403-1 -2
1.76 GPa

@Strain 3.50 %,
Temperature 23.0 °C
255 ksi

@Strain 3.50 %,
Temperature 73.4 °F
ISO 11403-1 -2
2.10 GPa

@Strain 1.20 %,
Temperature 40.0 °C
305 ksi

@Strain 1.20 %,
Temperature 104 °F
ISO 11403-1 -2
2.12 GPa

@Strain 4.40 %,
Temperature -40.0 °C
307 ksi

@Strain 4.40 %,
Temperature -40.0 °F
ISO 11403-1 -2
2.14 GPa

@Strain 3.20 %,
Temperature 0.000 °C
311 ksi

@Strain 3.20 %,
Temperature 32.0 °F
ISO 11403-1 -2
2.73 GPa

@Strain 0.900 %,
Temperature 23.0 °C
396 ksi

@Strain 0.900 %,
Temperature 73.4 °F
ISO 11403-1 -2
3.19 GPa

@Strain 1.40 %,
Temperature -20.0 °C
462 ksi

@Strain 1.40 %,
Temperature -4.00 °F
ISO 11403-1 -2
3.45 GPa

@Strain 0.800 %,
Temperature 0.000 °C
500 ksi

@Strain 0.800 %,
Temperature 32.0 °F
ISO 11403-1 -2
3.86 GPa

@Strain 1.10 %,
Temperature -40.0 °C
560 ksi

@Strain 1.10 %,
Temperature -40.0 °F
ISO 11403-1 -2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
Charpy Impact Unnotched 20.0 J/cm²
95.2 ft-lb/in²
ISO 179/1eU