DuPont Performance Polymers Hytrel® HTR8441 BK316 TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8441 BK316 TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® HTR8441 is a 55 nom. Shore D thermoplastic polyester elastomer for blow molding. It provides good mechanical properties at high temperature.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 10 g/10 min

@Load 10.0 kg,
Temperature 240 °C
10 g/10 min

@Load 22.0 lb,
Temperature 464 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 53

@Temperature 23.0 °C,
Time 15.0 sec
53

@Temperature 73.4 °F,
Time 0.00417 hour
ISO 868
Tensile Strength at Break 34.0 MPa

@Temperature 23.0 °C
4930 psi

@Temperature 73.4 °F
ISO 527 (1BA bar)
Tensile Stress 7.50 MPa

@Strain 5.00 %,
Temperature 23.0 °C
1090 psi

@Strain 5.00 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
11.6 MPa

@Strain 10.0 %,
Temperature 23.0 °C
1680 psi

@Strain 10.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
18.4 MPa

@Strain 50.0 %,
Temperature 23.0 °C
2670 psi

@Strain 50.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
Elongation at Break >= 50 %

@Temperature 23.0 °C
>= 50 %

@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)
390 %

@Temperature 23.0 °C
390 %

@Temperature 73.4 °F
nominal; ISO 527 (1BA bar)
400 %

@Temperature 23.0 °C
400 %

@Temperature 73.4 °F
ISO 527 (1BA bar)
Tensile Modulus 0.190 GPa

@Temperature 23.0 °C
27.6 ksi

@Temperature 73.4 °F
ISO 527
Charpy Impact, Notched 3.90 J/cm²

@Temperature -30.0 °C
18.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 213 °C
415 °F
10°C/min; ISO 11357-1/-3
Brittleness Temperature -62.0 °C
-79.6 °F
ISO 974
Processing Properties Metric English Comments
Melt Temperature 235 °C
455 °F
Optimum; Blow Molding
230 - 240 °C
446 - 464 °F
Blow Molding
Drying Temperature 110 °C
230 °F
Blow Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Blow Molding
Moisture Content <= 0.020 %
<= 0.020 %
Blow Molding
Descriptive Properties Value Comments
Appearance Black Color
Forms Pellets
Generic TPC
Material Status Preliminary Data
Part Marking Code >TPC-ET<
ISO 11469
Processing Method Blow Molding
Product Category Blow Moldable Resins
Region Available - Global Yes
Resin Identification TPC-ET
ISO 1043
RoHS Compliance Contact Manufacturer