DuPont Performance Polymers Hytrel® RS 40F3 NC010 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel® RS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® RS 40F3 NC010 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D Renewably Sourced High Flow Polyester Elastomer Developed for Injection Molding Hytrel RS 40F3 NC010 is a high flow low modulus grade containing at least 50% renewably sourced ingredients by weight. It is suitable for injection molding proceInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
0.0090 cm/cm
0.0090 in/in
48h at 80°C; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
0.0070 cm/cm
0.0070 in/in
48h at 80°C; ISO 294-4
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 220 °C
20 g/10 min

@Load 4.76 lb,
Temperature 428 °F
cm³/10min; ISO 1133
20 g/10 min

@Load 2.16 kg,
Temperature 220 °C
20 g/10 min

@Load 4.76 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 33
33
15s; ISO 868
<= 37
<= 37
ISO 868
Tensile Strength at Break 26.0 MPa
3770 psi
ISO 527-1/-2
Tensile Stress 2.10 MPa

@Strain 5.00 %
305 psi

@Strain 5.00 %
ISO 527-1/-2
3.30 MPa

@Strain 10.0 %
479 psi

@Strain 10.0 %
ISO 527-1/-2
6.50 MPa

@Strain 50.0 %
943 psi

@Strain 50.0 %
ISO 527-1/-2
Elongation at Break >= 300 %
>= 300 %
ISO 527-1/-2
800 %
800 %
Nominal; ISO 527-1/-2
Tensile Modulus 0.0450 GPa
6.53 ksi
ISO 527-1/-2
Flexural Modulus 0.0500 GPa
7.25 ksi
ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched NB
NB
ISO 179/1eA
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eA
NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ISO 179/1eA
Tear Strength 97.0 kN/m
553 pli
parallel; ISO 34-1
99.0 kN/m
565 pli
normal; ISO 34-1
Abrasion 200
200
mm³; ISO 4649
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 210 µm/m-°C
117 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 200 µm/m-°C
111 µin/in-°F
ISO 11359-1/-2
Melting Point 190 °C
374 °F
10°C/min; ISO 11357-1/-3
Brittleness Temperature -90.0 °C
-130 °F
ISO 974
-90.0 °C
-130 °F
ISO 6603-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
Oxygen Index 20 %
20 %
ISO 4589-1/-2
Descriptive Properties Value Comments
Delivery Form Pellets
Eff. thermal diffusivity 5.44E-08 m²/s
Part Marking Code >TPC-ET<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification TPC-ET
ISO 1043