DuPont Performance Polymers Rynite® 408 BK515 PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer	DuPont Performance Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Rynite® 408 BK515 PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Rynite® 408 BK515 is a 30% glass reinforced modified polyethylene terephthalate with improved impact resistance. Excellent balance of strength, stiffness, toughness and temperature resistance.Information provided by DuPont

Physical Properties	Metric	English	Comments
Density	1.49 g/cc	0.0538 lb/in³	ISO 1183
Filler Content	30 %	30 %

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa @Temperature 150 °C	7980 psi @Temperature 302 °F	ISO 527
	71.0 MPa @Temperature 90.0 °C	10300 psi @Temperature 194 °F	ISO 527
	127 MPa @Temperature 23.0 °C	18400 psi @Temperature 73.4 °F	ISO 527
	179 MPa @Temperature -40.0 °C	26000 psi @Temperature -40.0 °F	ISO 527
Elongation at Break	2.6 % @Temperature -40.0 °C	2.6 % @Temperature -40.0 °F	ISO 527
	2.9 % @Temperature 23.0 °C	2.9 % @Temperature 73.4 °F	ISO 527
	9.7 % @Temperature 90.0 °C	9.7 % @Temperature 194 °F	ISO 527
	11 % @Temperature 150 °C	11 % @Temperature 302 °F	ISO 527
Tensile Modulus	2.89 GPa @Temperature 150 °C	419 ksi @Temperature 302 °F	ISO 527
	4.02 GPa @Temperature 90.0 °C	583 ksi @Temperature 194 °F	ISO 527
	9.30 GPa @Temperature 23.0 °C	1350 ksi @Temperature 73.4 °F	ISO 527
	10.79 GPa @Temperature -40.0 °C	1565 ksi @Temperature -40.0 °F	ISO 527
Flexural Modulus	7.962 GPa @Temperature 23.0 °C	1155 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/m² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	6.40 J/cm² @Temperature 23.0 °C	30.5 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	250 °C	482 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	237 °C	459 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	218 °C	424 °F	ISO 75-1/-2
UL RTI, Electrical	140 °C @Thickness 0.750 mm	284 °F @Thickness 0.0295 in	UL 746B
UL RTI, Mechanical with Impact	140 °C @Thickness 0.750 mm	284 °F @Thickness 0.0295 in	UL 746B
UL RTI, Mechanical without Impact	140 °C @Thickness 0.750 mm	284 °F @Thickness 0.0295 in	UL 746B
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	UL94

Processing Properties	Metric	English	Comments
Melt Temperature	280 °C	536 °F	Optimum
	270 - 290 °C	518 - 554 °F
Mold Temperature	>= 95.0 °C	>= 203 °F
	110 °C	230 °F	Optimum
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour	Dehumidified Dryer
Moisture Content	<= 0.020 %	<= 0.020 %

Descriptive Properties	Value	Comments
Appearance	Black Color
Drying Recommended	Yes
Features	Creep Resistance, Good
	Dimensional Stability, Good
	Electrical Properties, Good
	Stiffness, Good
	Strength, Good
	Thermal Aging Resistance, Good
Filler	Glass fiber reinforcement
	Glass Reinforced
Generic	PET
Material Status	Current
Part Marking Code	>PET-IGF30<	ISO 11469
Processing Method	Injection Molding
Product Category	Glass Reinforced Resins
	Toughened Resins
Region Available - Americas	Yes
Region Available - Asia/Pacific	Yes
Region Available - Europe	Yes
Resin Identification	PET-IGF30	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Automotive Applications
	Electrical/Electronic Applications
	Housings
	Phenolic Replacement
	Structural Parts