DuPont Performance Polymers Rynite® 515CS BK575M PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® 515CS BK575M PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® 515CS BK575M is a 15% glass fiber reinforced, black polyethylene terephthalate resin modified for improved color stability after heat aging.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Filler Content 15 %
15 %
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
0.0020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Thickness 2.00 mm
0.0090 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 97.0 MPa

@Temperature 23.0 °C
14100 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 2.4 %

@Temperature 23.0 °C
2.4 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 6.20 GPa

@Temperature 23.0 °C
899 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 5.60 GPa

@Temperature 23.0 °C
812 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
5.00 kJ/m²

@Temperature -40.0 °C
2.38 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
Charpy Impact Unnotched 2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
0.500 J/cm²

@Temperature -40.0 °C
2.38 ft-lb/in²

@Temperature -40.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 250 °C
482 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
UL RTI, Electrical 75.0 °C

@Thickness 0.750 mm
167 °F

@Thickness 0.0295 in
UL 746B
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.750 mm
167 °F

@Thickness 0.0295 in
UL 746B
UL RTI, Mechanical without Impact 75.0 °C

@Thickness 0.750 mm
167 °F

@Thickness 0.0295 in
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
Oxygen Index 20 %
20 %
ISO 4589-1/-2
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
Optimum
Mold Temperature 130 - 140 °C
266 - 284 °F
135 °C
275 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Appearance Black Color
Drying Recommended Yes
Filler Glass Reinforced
Generic PET
Material Status Current
Part Marking Code >PET-GF15<
ISO 11469
Polymer Family Polyester
Polymer Type PET
Product Category Color Stable Resins
Glass Reinforced Resins
Resin Identification PET-GF15
ISO 1043
RoHS Compliance Contact Manufacturer