DuPont Performance Polymers Rynite® FR515 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR515 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Flame Retardant Polyethylene Terephthalate Rynite FR515 NC010 is a flame retardant 15% glass reinforced modified polyethylene terephthalate. Recognized by UL as UL94V-0 at 0.8mm(0.03in). Has a 140C temp index. Excellent balance ofInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Viscosity 658000 cP

@Shear Rate 12.0 1/s,
Temperature 295 °C
 658000 cP

@Shear Rate 12.0 1/s,
Temperature 563 °F
 ISO 11403-1 -2
998000 cP

@Shear Rate 12.0 1/s,
Temperature 285 °C
 998000 cP

@Shear Rate 12.0 1/s,
Temperature 545 °F
 ISO 11403-1 -2
1.33e+6 cP

@Shear Rate 12.0 1/s,
Temperature 275 °C
 1.33e+6 cP

@Shear Rate 12.0 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
0.0050 cm/cm
0.0050 in/in
annealed; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
0.0115 cm/cm
0.0115 in/in
annealed; ISO 294-4
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 6.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 88
88
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Strength at Break 107 MPa
15500 psi
ISO 527-1/-2
Tensile Stress 16.13 MPa

@Strain 0.460 %,
Temperature 90.0 °C
 2339 psi

@Strain 0.460 %,
Temperature 194 °F
 ISO 11403-1 -2
17.35 MPa

@Strain 0.260 %,
Temperature 40.0 °C
 2516 psi

@Strain 0.260 %,
Temperature 104 °F
 ISO 11403-1 -2
20.0 MPa

@Strain 0.270 %,
Temperature 23.0 °C
 2900 psi

@Strain 0.270 %,
Temperature 73.4 °F
 ISO 11403-1 -2
46.19 MPa

@Strain 1.81 %,
Temperature 90.0 °C
 6699 psi

@Strain 1.81 %,
Temperature 194 °F
 ISO 11403-1 -2
59.46 MPa

@Strain 3.16 %,
Temperature 90.0 °C
 8624 psi

@Strain 3.16 %,
Temperature 194 °F
 ISO 11403-1 -2
60.81 MPa

@Strain 4.52 %,
Temperature 90.0 °C
 8820 psi

@Strain 4.52 %,
Temperature 194 °F
 ISO 11403-1 -2
61.0 MPa

@Strain 1.04 %,
Temperature 40.0 °C
 8850 psi

@Strain 1.04 %,
Temperature 104 °F
 ISO 11403-1 -2
66.0 MPa

@Strain 1.04 %,
Temperature 23.0 °C
 9570 psi

@Strain 1.04 %,
Temperature 73.4 °F
 ISO 11403-1 -2
87.6 MPa

@Strain 1.82 %,
Temperature 40.0 °C
 12700 psi

@Strain 1.82 %,
Temperature 104 °F
 ISO 11403-1 -2
97.08 MPa

@Strain 1.83 %,
Temperature 23.0 °C
 14080 psi

@Strain 1.83 %,
Temperature 73.4 °F
 ISO 11403-1 -2
100.6 MPa

@Strain 2.60 %,
Temperature 40.0 °C
 14590 psi

@Strain 2.60 %,
Temperature 104 °F
 ISO 11403-1 -2
113.1 MPa

@Strain 2.61 %,
Temperature 23.0 °C
 16400 psi

@Strain 2.61 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Elongation at Break 2.6 %
2.6 %
ISO 527-1/-2
Tensile Modulus 6.80 GPa
986 ksi
ISO 527-1/-2
0.269 GPa

@Temperature 230 °C
 39.0 ksi

@Temperature 446 °F
 Dynamic; ISO 11403-1 -2
0.467 GPa

@Temperature 170 °C
 67.7 ksi

@Temperature 338 °F
 Dynamic; ISO 11403-1 -2
0.736 GPa

@Temperature 90.0 °C
 107 ksi

@Temperature 194 °F
 Dynamic; ISO 11403-1 -2
1.495 GPa

@Temperature 40.0 °C
 216.8 ksi

@Temperature 104 °F
 Dynamic; ISO 11403-1 -2
1.849 GPa

@Temperature -20.0 °C
 268.2 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
2.01 GPa

@Temperature -50.0 °C
 292 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Flexural Strength 170 MPa
24700 psi
ISO 178
Flexural Modulus 5.94 GPa
862 ksi
ISO 178
Shear Strength 0.007896 MPa

@Shear Rate 12.0 1/s,
Temperature 295 °C
 1.145 psi

@Shear Rate 12.0 1/s,
Temperature 563 °F
 ISO 11403-1 -2
0.008556 MPa

@Shear Rate 7.00 1/s,
Temperature 285 °C
 1.241 psi

@Shear Rate 7.00 1/s,
Temperature 545 °F
 ISO 11403-1 -2
0.011753 MPa

@Shear Rate 7.00 1/s,
Temperature 275 °C
 1.7046 psi

@Shear Rate 7.00 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Secant Modulus 4.47 GPa

@Strain 2.08 %,
Temperature 40.0 °C
 649 ksi

@Strain 2.08 %,
Temperature 104 °F
 ISO 11403-1 -2
4.95 GPa

@Strain 2.09 %,
Temperature 23.0 °C
 718 ksi

@Strain 2.09 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.87 GPa

@Strain 1.04 %,
Temperature 40.0 °C
 851 ksi

@Strain 1.04 %,
Temperature 104 °F
 ISO 11403-1 -2
6.35 GPa

@Strain 1.04 %,
Temperature 23.0 °C
 920 ksi

@Strain 1.04 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.67 GPa

@Strain 0.260 %,
Temperature 40.0 °C
 968 ksi

@Strain 0.260 %,
Temperature 104 °F
 ISO 11403-1 -2
7.41 GPa

@Strain 0.270 %,
Temperature 23.0 °C
 1070 ksi

@Strain 0.270 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
2.00 J/cm²

@Temperature -40.0 °C
 9.52 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -40.0 °C
 3.33 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C
10.0 µin/in-°F
ISO 11359-1/-2
12.0 µm/m-°C

@Temperature 55.0 - 160 °C
 6.67 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
33.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 18.3 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 88.0 µm/m-°C
48.9 µin/in-°F
ISO 11359-1/-2
70.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
3.1

@Frequency 1000 Hz
 3.1

@Frequency 1000 Hz
 ASTM D150
3.7

@Frequency 100 Hz
 3.7

@Frequency 100 Hz
 IEC 60250
3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1000 Hz
 0.0040

@Frequency 1000 Hz
 ASTM D150
0.0090

@Frequency 100 Hz
 0.0090

@Frequency 100 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 ASTM D150
Comparative Tracking Index 200 V
200 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A