DuPont Performance Polymers Rynite® FR530L BK507 PET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR530L BK507 PET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® FR530L BK507 is a 30% glass reinforced, flame retardant, modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Filler Content 30 %
30 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 133 MPa

@Temperature 23.0 °C
19300 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 1.9 %

@Temperature 23.0 °C
1.9 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 11.3 GPa

@Temperature 23.0 °C
1640 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 10.5 GPa

@Temperature 23.0 °C
1520 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 8.50 kJ/m²

@Temperature 23.0 °C
4.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 252 °C
486 °F
10°C/min; ISO 11357-1/-3
UL RTI, Electrical 155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 0.750 mm
311 °F

@Thickness 0.0295 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
155 °C

@Thickness 0.350 mm
311 °F

@Thickness 0.0138 in
UL 746B
UL RTI, Mechanical with Impact 155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 0.750 mm
311 °F

@Thickness 0.0295 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
UL RTI, Mechanical without Impact 155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 3.00 mm
311 °F

@Thickness 0.118 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 1.50 mm
311 °F

@Thickness 0.0591 in
UL 746B
155 °C

@Thickness 0.750 mm
311 °F

@Thickness 0.0295 in
UL 746B
155 °C

@Thickness 2.00 mm
311 °F

@Thickness 0.0787 in
UL 746B
Flammability, UL94 V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
IEC 60695-11-10
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
IEC 60695-11-10
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
IEC 60695-11-10
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
V-0

@Thickness 0.350 mm
V-0

@Thickness 0.0138 in
IEC 60695-11-10
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL94
V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL94
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL94
V-0

@Thickness 0.350 mm
V-0

@Thickness 0.0138 in
UL94
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
IEC 60695-11-20
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
IEC 60695-11-10
5VA

@Thickness 2.00 mm
5VA

@Thickness 0.0787 in
IEC 60695-11-10
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
IEC 60695-11-10
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL94
5VA

@Thickness 2.00 mm
5VA

@Thickness 0.0787 in
UL94
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
UL94
Glow Wire Test 800 °C

@Thickness 0.750 mm
1470 °F

@Thickness 0.0295 in
Ignition; IEC 60695-2-13
800 °C

@Thickness 1.50 mm
1470 °F

@Thickness 0.0591 in
Ignition; IEC 60695-2-13
800 °C

@Thickness 1.50 mm
1470 °F

@Thickness 0.0591 in
Ignition; IEC 60695-2-13
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
IEC 60695-2-12
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
IEC 60695-2-12
985 °C

@Thickness 2.00 mm
1810 °F

@Thickness 0.0787 in
Ignition; IEC 60695-2-13
985 °C

@Thickness 2.00 mm
1810 °F

@Thickness 0.0787 in
Ignition; IEC 60695-2-13
985 °C

@Thickness 3.00 mm
1810 °F

@Thickness 0.118 in
Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Comparative Tracking Index 200 V

@Temperature 23.0 °C
200 V

@Temperature 73.4 °F
IEC 60112
250 V

@Temperature 23.0 °C
250 V

@Temperature 73.4 °F
UL 746A
250 - 400 V

@Temperature 23.0 °C
250 - 400 V

@Temperature 73.4 °F
UL 746A
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Optimum
270 - 290 °C
518 - 554 °F
Mold Temperature 90.0 - 110 °C
194 - 230 °F
110 °C
230 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Appearance Black Color
Drying Recommended Yes
Filler Glass Reinforced
Forms Pellets
Generic PET
Material Status Current
Part Marking Code >PET-GF30FR(17)<
ISO 11469
Polymer Family Polyester