DuPont Performance Polymers Rynite® RE5329 BK503 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® RE5329 BK503 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
36% Glass Reinforced Polyethylene TerephthalateInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Tensile Stress 6.22 MPa

@Strain 0.230 %,
Temperature 150 °C
 902 psi

@Strain 0.230 %,
Temperature 302 °F
 ISO 11403-1 -2
12.27 MPa

@Strain 0.250 %,
Temperature 90.0 °C
 1780 psi

@Strain 0.250 %,
Temperature 194 °F
 ISO 11403-1 -2
19.58 MPa

@Strain 1.15 %,
Temperature 150 °C
 2840 psi

@Strain 1.15 %,
Temperature 302 °F
 ISO 11403-1 -2
25.86 MPa

@Strain 2.40 %,
Temperature 150 °C
 3751 psi

@Strain 2.40 %,
Temperature 302 °F
 ISO 11403-1 -2
25.99 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 3770 psi

@Strain 0.230 %,
Temperature 73.4 °F
 ISO 11403-1 -2
28.28 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 4102 psi

@Strain 0.230 %,
Temperature -4.00 °F
 ISO 11403-1 -2
28.28 MPa

@Strain 0.230 %,
Temperature 0.000 °C
 4102 psi

@Strain 0.230 %,
Temperature 32.0 °F
 ISO 11403-1 -2
28.63 MPa

@Strain 3.80 %,
Temperature 150 °C
 4152 psi

@Strain 3.80 %,
Temperature 302 °F
 ISO 11403-1 -2
29.16 MPa

@Strain 0.230 %,
Temperature 40.0 °C
 4229 psi

@Strain 0.230 %,
Temperature 104 °F
 ISO 11403-1 -2
33.79 MPa

@Strain 1.00 %,
Temperature 90.0 °C
 4901 psi

@Strain 1.00 %,
Temperature 194 °F
 ISO 11403-1 -2
44.27 MPa

@Strain 1.93 %,
Temperature 90.0 °C
 6421 psi

@Strain 1.93 %,
Temperature 194 °F
 ISO 11403-1 -2
49.83 MPa

@Strain 3.11 %,
Temperature 90.0 °C
 7227 psi

@Strain 3.11 %,
Temperature 194 °F
 ISO 11403-1 -2
54.87 MPa

@Strain 0.510 %,
Temperature 23.0 °C
 7958 psi

@Strain 0.510 %,
Temperature 73.4 °F
 ISO 11403-1 -2
55.86 MPa

@Strain 0.480 %,
Temperature 40.0 °C
 8102 psi

@Strain 0.480 %,
Temperature 104 °F
 ISO 11403-1 -2
57.86 MPa

@Strain 0.470 %,
Temperature -20.0 °C
 8392 psi

@Strain 0.470 %,
Temperature -4.00 °F
 ISO 11403-1 -2
63.22 MPa

@Strain 0.530 %,
Temperature 0.000 °C
 9169 psi

@Strain 0.530 %,
Temperature 32.0 °F
 ISO 11403-1 -2
76.51 MPa

@Strain 0.830 %,
Temperature 40.0 °C
 11100 psi

@Strain 0.830 %,
Temperature 104 °F
 ISO 11403-1 -2
77.76 MPa

@Strain 0.830 %,
Temperature 23.0 °C
 11280 psi

@Strain 0.830 %,
Temperature 73.4 °F
 ISO 11403-1 -2
85.86 MPa

@Strain 0.750 %,
Temperature -20.0 °C
 12450 psi

@Strain 0.750 %,
Temperature -4.00 °F
 ISO 11403-1 -2
89.19 MPa

@Strain 0.870 %,
Temperature 0.000 °C
 12940 psi

@Strain 0.870 %,
Temperature 32.0 °F
 ISO 11403-1 -2
90.66 MPa

@Strain 1.42 %,
Temperature 40.0 °C
 13150 psi

@Strain 1.42 %,
Temperature 104 °F
 ISO 11403-1 -2
96.37 MPa

@Strain 1.27 %,
Temperature 23.0 °C
 13980 psi

@Strain 1.27 %,
Temperature 73.4 °F
 ISO 11403-1 -2
110.83 MPa

@Strain 1.41 %,
Temperature 0.000 °C
 16075 psi

@Strain 1.41 %,
Temperature 32.0 °F
 ISO 11403-1 -2
112.06 MPa

@Strain 1.19 %,
Temperature -20.0 °C
 16253 psi

@Strain 1.19 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 2.2 %
2.2 %
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527-1/-2
Secant Modulus 4.7735 GPa

@Strain 2.00 %,
Temperature 40.0 °C
 692.35 ksi

@Strain 2.00 %,
Temperature 104 °F
 ISO 11403-1 -2
6.33 GPa

@Strain 1.66 %,
Temperature 23.0 °C
 918 ksi

@Strain 1.66 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.92 GPa

@Strain 1.59 %,
Temperature -20.0 °C
 1150 ksi

@Strain 1.59 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.21 GPa

@Strain 1.00 %,
Temperature 40.0 °C
 1190 ksi

@Strain 1.00 %,
Temperature 104 °F
 ISO 11403-1 -2
8.87 GPa

@Strain 0.950 %,
Temperature 23.0 °C
 1290 ksi

@Strain 0.950 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.4951 GPa

@Strain 1.02 %,
Temperature 0.000 °C
 1377.2 ksi

@Strain 1.02 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.7 GPa

@Strain 0.890 %,
Temperature -20.0 °C
 1560 ksi

@Strain 0.890 %,
Temperature -4.00 °F
 ISO 11403-1 -2
10.8 GPa

@Strain 0.510 %,
Temperature 23.0 °C
 1560 ksi

@Strain 0.510 %,
Temperature 73.4 °F
 ISO 11403-1 -2
11.3 GPa

@Strain 0.230 %,
Temperature 23.0 °C
 1640 ksi

@Strain 0.230 %,
Temperature 73.4 °F
 ISO 11403-1 -2
11.6 GPa

@Strain 0.480 %,
Temperature 40.0 °C
 1690 ksi

@Strain 0.480 %,
Temperature 104 °F
 ISO 11403-1 -2
11.9 GPa

@Strain 0.530 %,
Temperature 0.000 °C
 1730 ksi

@Strain 0.530 %,
Temperature 32.0 °F
 ISO 11403-1 -2
12.3 GPa

@Strain 0.230 %,
Temperature 0.000 °C
 1780 ksi

@Strain 0.230 %,
Temperature 32.0 °F
 ISO 11403-1 -2
12.3 GPa

@Strain 0.230 %,
Temperature -20.0 °C
 1780 ksi

@Strain 0.230 %,
Temperature -4.00 °F
 ISO 11403-1 -2
12.3 GPa

@Strain 0.470 %,
Temperature -20.0 °C
 1790 ksi

@Strain 0.470 %,
Temperature -4.00 °F
 ISO 11403-1 -2
12.7 GPa

@Strain 0.230 %,
Temperature 40.0 °C
 1840 ksi

@Strain 0.230 %,
Temperature 104 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 2.10 J/cm²
9.99 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.340 J/cm²
1.62 ft-lb/in²
ISO 179/1eA
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America