| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8550 (GFLT-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationVTR-8550
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 64 @Temperature 121 °C |
64 @Temperature 250 °F |
ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.3 MPa | 2650 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 207 % | 207 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00660 GPa | 0.957 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C |
11 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -23.9 °C | -11.0 °F | TR-10 |
| Glass Transition Temp, Tg | -25.7 °C | -14.3 °F | DSC |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EHB400A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA), 65% GlassMineral (Dry)
- Plenco 00732 Melamine-Phenolic, Granular, Injection Molded
- Universal Wire Works 316 Stainless Steel (AMS 5692) Filler Metal
- A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate
- Covestro Makrolon® 8035 Polycarbonate
- ExxonMobil Escorene™ UL 12530CC Ethylene Vinyl Acetate Copolymer (European Grade)
- Carpenter 20Cb-3® Stainless Steel, Strip, Annealed at 1750°F (955°C) then Water Quenched
- BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved