DuPont Performance Polymers Zytel® 158 NC010 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 158 NC010 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Polyamide 612Zytel 158 NC010 is an intermediate viscosity PA 612 resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
1.06 g/cc
0.0383 lb/in³
DAM; ISO 1183
Water Absorption 3.0 %

@Thickness 2.00 mm
3.0 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Moisture Absorption 1.30 %

@Thickness 2.00 mm
1.30 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Viscosity 54050 cP

@Shear Rate 5000 1/s,
Temperature 290 °C
54050 cP

@Shear Rate 5000 1/s,
Temperature 554 °F
ISO 11403-1 -2
74410 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
74410 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11403-1 -2
88620 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
88620 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
ISO 11403-1 -2
116500 cP

@Shear Rate 500 1/s,
Temperature 290 °C
116500 cP

@Shear Rate 500 1/s,
Temperature 554 °F
ISO 11403-1 -2
140700 cP

@Shear Rate 10.0 1/s,
Temperature 290 °C
140700 cP

@Shear Rate 10.0 1/s,
Temperature 554 °F
ISO 11403-1 -2
197900 cP

@Shear Rate 500 1/s,
Temperature 250 °C
197900 cP

@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11403-1 -2
262900 cP

@Shear Rate 500 1/s,
Temperature 230 °C
262900 cP

@Shear Rate 500 1/s,
Temperature 446 °F
ISO 11403-1 -2
274600 cP

@Shear Rate 10.0 1/s,
Temperature 250 °C
274600 cP

@Shear Rate 10.0 1/s,
Temperature 482 °F
ISO 11403-1 -2
408300 cP

@Shear Rate 10.0 1/s,
Temperature 230 °C
408300 cP

@Shear Rate 10.0 1/s,
Temperature 446 °F
ISO 11403-1 -2
Viscosity Test 120 cm³/g
120 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
DAM; ISO 294-4 2577
0.011 cm/cm

@Thickness 3.20 mm
0.011 in/in

@Thickness 0.126 in
DAM
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
DAM; ISO 294-4 2577
0.011 cm/cm

@Thickness 3.20 mm
0.011 in/in

@Thickness 0.126 in
DAM; ASTM D149
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
50%RH; ISO 2039-2
114
114
DAM; ISO 2039-2
Tensile Stress 9.30 MPa

@Strain 2.55 %,
Temperature 90.0 °C
1350 psi

@Strain 2.55 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
10.0 MPa

@Strain 2.57 %,
Temperature 90.0 °C
1450 psi

@Strain 2.57 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
11.2 MPa

@Strain 0.380 %,
Temperature 23.0 °C
1620 psi

@Strain 0.380 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
14.0 MPa

@Strain 0.450 %,
Temperature 0.000 °C
2030 psi

@Strain 0.450 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
16.0 MPa

@Strain 2.30 %,
Temperature 40.0 °C
2320 psi

@Strain 2.30 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
20.6 MPa

@Strain 10.3 %,
Temperature 90.0 °C
2990 psi

@Strain 10.3 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
22.3 MPa

@Strain 10.2 %,
Temperature 90.0 °C
3230 psi

@Strain 10.2 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
23.2 MPa

@Strain 18.0 %,
Temperature 90.0 °C
3360 psi

@Strain 18.0 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
24.3 MPa

@Strain 25.7 %,
Temperature 90.0 °C
3520 psi

@Strain 25.7 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
24.8 MPa

@Strain 17.9 %,
Temperature 90.0 °C
3600 psi

@Strain 17.9 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
25.9 MPa

@Strain 25.5 %,
Temperature 90.0 °C
3760 psi

@Strain 25.5 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
26.8 MPa

@Strain 1.85 %,
Temperature 23.0 °C
3890 psi

@Strain 1.85 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
30.0 MPa

@Strain 1.15 %,
Temperature -20.0 °C
4350 psi

@Strain 1.15 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
32.0 MPa

@Strain 5.60 %,
Temperature 40.0 °C
4640 psi

@Strain 5.60 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
34.6 MPa

@Strain 1.45 %,
Temperature 0.000 °C
5020 psi

@Strain 1.45 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
35.9 MPa

@Strain 9.20 %,
Temperature 40.0 °C
5210 psi

@Strain 9.20 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
36.9 MPa

@Strain 1.52 %,
Temperature 23.0 °C
5350 psi

@Strain 1.52 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
39.1 MPa

@Strain 16.1 %,
Temperature 40.0 °C
5670 psi

@Strain 16.1 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
40.1 MPa

@Strain 23.0 %,
Temperature 40.0 °C
5820 psi

@Strain 23.0 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
42.8 MPa

@Strain 13.4 %,
Temperature 40.0 °C
6210 psi

@Strain 13.4 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
44.9 MPa

@Strain 21.2 %,
Temperature 40.0 °C
6510 psi

@Strain 21.2 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
44.9 MPa

@Strain 7.40 %,
Temperature 23.0 °C
6510 psi

@Strain 7.40 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
46.0 MPa

@Strain 29.0 %,
Temperature 40.0 °C
6670 psi

@Strain 29.0 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
46.7 MPa

@Strain 1.80 %,
Temperature 0.000 °C
6770 psi

@Strain 1.80 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
48.0 MPa

@Strain 13.0 %,
Temperature 23.0 °C
6960 psi

@Strain 13.0 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
49.5 MPa

@Strain 18.5 %,
Temperature 23.0 °C
7180 psi

@Strain 18.5 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
51.8 MPa

@Strain 2.66 %,
Temperature 23.0 °C
7510 psi

@Strain 2.66 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
56.8 MPa

@Strain 3.80 %,
Temperature 23.0 °C
8240 psi

@Strain 3.80 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
63.1 MPa

@Strain 5.80 %,
Temperature 0.000 °C
9150 psi

@Strain 5.80 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
65.3 MPa

@Strain 10.2 %,
Temperature 0.000 °C
9470 psi

@Strain 10.2 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
66.0 MPa

@Strain 14.5 %,
Temperature 0.000 °C
9570 psi

@Strain 14.5 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
66.8 MPa

@Strain 3.15 %,
Temperature 0.000 °C
9690 psi

@Strain 3.15 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
68.0 MPa

@Strain 4.60 %,
Temperature -20.0 °C
9860 psi

@Strain 4.60 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
73.1 MPa

@Strain 4.50 %,
Temperature 0.000 °C
10600 psi

@Strain 4.50 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
73.4 MPa

@Strain 8.05 %,
Temperature -20.0 °C
10600 psi

@Strain 8.05 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
74.0 MPa

@Strain 11.5 %,
Temperature -20.0 °C
10700 psi

@Strain 11.5 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
Tensile Strength, Yield 52.0 MPa
7540 psi
50%RH; ISO 527-1/-2
62.0 MPa
8990 psi
DAM; ISO 527-1/-2
Elongation at Break 35 %
35 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 4.3 %
4.3 %
DAM; ISO 527-1/-2
4.3 %
4.3 %
DAM; ISO 527-3
19 %
19 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.50 GPa
218 ksi
50%RH; ISO 527-1/-2
2.40 GPa
348 ksi
DAM; ISO 527-1/-2
1.30 GPa

@Temperature 50.0 °C
189 ksi

@Temperature 122 °F
DAM; Dynamic; ISO 11403-1 -2
3.90 GPa

@Temperature -100 °C
566 ksi

@Temperature -148 °F
DAM; Dynamic; ISO 11403-1 -2
Shear Strength 0.001407 MPa

@Shear Rate 10.0 1/s,
Temperature 290 °C
0.2041 psi

@Shear Rate 10.0 1/s,
Temperature 554 °F
ISO 11403-1 -2