DuPont Performance Polymers Zytel® 70G30L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G30L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® 70G30L NC010 is a 30% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
DAM; ISO 1183
Filler Content 30 %
30 %
DAM
Water Absorption 2.0 %

@Thickness 1.00 mm,
Temperature 23.0 °C
2.0 %

@Thickness 0.0394 in,
Temperature 73.4 °F
Equilibrium 50%RH; DAM; ISO 62, Similar to
6.9 %

@Thickness 1.00 mm,
Temperature 23.0 °C
6.9 %

@Thickness 0.0394 in,
Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
0.0030 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 2.00 mm
0.011 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa

@Temperature 23.0 °C
18900 psi

@Temperature 73.4 °F
50%RH; ISO 527
195 MPa

@Temperature 23.0 °C
28300 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 3.5 %

@Temperature 23.0 °C
3.5 %

@Temperature 73.4 °F
DAM; ISO 527
5.0 %

@Temperature 23.0 °C
5.0 %

@Temperature 73.4 °F
50%RH; ISO 527
Tensile Modulus 7.20 GPa

@Temperature 23.0 °C
1040 ksi

@Temperature 73.4 °F
50%RH; ISO 527
9.80 GPa

@Temperature 23.0 °C
1420 ksi

@Temperature 73.4 °F
DAM; ISO 527
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1A
14.0 kJ/m²

@Temperature 23.0 °C
6.66 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 180/1A
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
9.30 J/cm²

@Temperature 23.0 °C
44.3 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 253 °C
487 °F
DAM; ISO 75-1/-2
Glass Transition Temp, Tg 80.0 °C
176 °F
10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical 130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
DAM; UL 746B
130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
DAM; UL 746B
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
DAM; UL 746B
UL RTI, Mechanical with Impact 120 °C

@Thickness 0.710 mm
248 °F

@Thickness 0.0280 in
DAM; UL 746B
120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
DAM; UL 746B
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
DAM; UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
DAM; UL 746B
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
DAM; UL 746B
130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
DAM; UL 746B
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; UL94
HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
DAM; UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
DAM; IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; IEC 60695-11-10
Oxygen Index 24 %
24 %
DAM; ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm

@Temperature 23.0 °C
1.00e+13 ohm-cm

@Temperature 73.4 °F
DAM; IEC 60093
Surface Resistance 1.00e+12 ohm

@Temperature 23.0 °C
1.00e+12 ohm

@Temperature 73.4 °F
50%RH; IEC 60093
Dissipation Factor 0.016

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.016

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
DAM; IEC 60250
0.016

@Frequency 100 Hz,
Temperature 23.0 °C
0.016

@Frequency 100 Hz,
Temperature 73.4 °F
DAM; IEC 60250
Comparative Tracking Index >= 600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
>= 600 V

@Thickness 0.118 in,
Temperature 73.4 °F
DAM; UL 746A
600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
600 V

@Thickness 0.118 in,
Temperature 73.4 °F
DAM; UL 746A
Processing Properties Metric English Comments
Melt Temperature 295 °C
563 °F
DAM; Optimum
285 - 305 °C
545 - 581 °F
DAM
Mold Temperature 70.0 - 120 °C
158 - 248 °F
DAM
100 °C
212 °F
DAM; optimum
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Appearance Natural Color
DAM
Drying Recommended Yes, if moisture content of resin exceeds recommended level
DAM
Features Chemical Resistance, Good
DAM
Creep Resistance, Good
DAM
Fatigue Resistant
DAM
Fuel Resistant
DAM
General Purpose
DAM
Grease Resistant
DAM
Lubricated
DAM
Oil Resistant
DAM
Stiffness, High
DAM
Strength, High
DAM
Filler Glass fiber reinforcement
DAM
Forms Pellets
DAM
Generic Nylon 66
DAM
Material Status Current
DAM
Part Marking Code >PA66-GF30<
ISO 11469; DAM
Polymer Family Polyamide
DAM
Polymer Type PA66
DAM
Processing Method Injection Molding
DAM
Product Category Glass Reinforced Resins
DAM
Glass Reinforced Resins
DAM
Region Available - Global Yes
DAM
Resin Identification PA66-GF30
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM
Uses Appliance Components
DAM
Automotive Applications
DAM
Electrical/Electronic Applications
DAM
Industrial Applications
DAM