DuPont Performance Polymers Zytel® 70G35HSLRA4 BK267 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G35HSLRA4 BK267 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® 70G35HSLRA4 BK267 is a 35% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding. It has excellent flow characteristics.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
DAM; ISO 1183
Filler Content 35 %
35 %
DAM
Water Absorption 1.7 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 1.7 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
5.5 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 5.5 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
 0.0040 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 2.00 mm
 0.011 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa

@Temperature 23.0 °C
 20300 psi

@Temperature 73.4 °F
 50%RH; ISO 527
210 MPa

@Temperature 23.0 °C
 30500 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 22.88 MPa

@Strain 0.520 %,
Temperature 150 °C
 3318 psi

@Strain 0.520 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
23.42 MPa

@Strain 0.450 %,
Temperature 120 °C
 3397 psi

@Strain 0.450 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
27.68 MPa

@Strain 0.480 %,
Temperature 90.0 °C
 4015 psi

@Strain 0.480 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
30.57 MPa

@Strain 0.400 %,
Temperature 60.0 °C
 4434 psi

@Strain 0.400 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
38.82 MPa

@Strain 1.00 %,
Temperature 150 °C
 5630 psi

@Strain 1.00 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
41.19 MPa

@Strain 0.900 %,
Temperature 120 °C
 5974 psi

@Strain 0.900 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
48.49 MPa

@Strain 0.950 %,
Temperature 90.0 °C
 7033 psi

@Strain 0.950 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
51.08 MPa

@Strain 1.51 %,
Temperature 150 °C
 7409 psi

@Strain 1.51 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
54.97 MPa

@Strain 1.35 %,
Temperature 120 °C
 7973 psi

@Strain 1.35 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
56.67 MPa

@Strain 0.810 %,
Temperature 60.0 °C
 8219 psi

@Strain 0.810 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
60.67 MPa

@Strain 2.02 %,
Temperature 150 °C
 8799 psi

@Strain 2.02 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
65.07 MPa

@Strain 1.42 %,
Temperature 90.0 °C
 9438 psi

@Strain 1.42 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
65.1 MPa

@Strain 0.670 %,
Temperature 40.0 °C
 9440 psi

@Strain 0.670 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
66.75 MPa

@Strain 1.81 %,
Temperature 120 °C
 9681 psi

@Strain 1.81 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
68.19 MPa

@Strain 2.51 %,
Temperature 150 °C
 9890 psi

@Strain 2.51 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
74.22 MPa

@Strain 3.01 %,
Temperature 150 °C
 10760 psi

@Strain 3.01 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
76.15 MPa

@Strain 2.26 %,
Temperature 120 °C
 11040 psi

@Strain 2.26 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
76.53 MPa

@Strain 1.20 %,
Temperature 60.0 °C
 11100 psi

@Strain 1.20 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
78.75 MPa

@Strain 3.50 %,
Temperature 150 °C
 11420 psi

@Strain 3.50 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
79.19 MPa

@Strain 1.89 %,
Temperature 90.0 °C
 11490 psi

@Strain 1.89 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
81.91 MPa

@Strain 4.01 %,
Temperature 150 °C
 11880 psi

@Strain 4.01 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
83.72 MPa

@Strain 2.71 %,
Temperature 120 °C
 12140 psi

@Strain 2.71 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
83.83 MPa

@Strain 4.51 %,
Temperature 150 °C
 12160 psi

@Strain 4.51 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
84.2 MPa

@Strain 5.00 %,
Temperature 150 °C
 12200 psi

@Strain 5.00 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
89.92 MPa

@Strain 3.16 %,
Temperature 120 °C
 13040 psi

@Strain 3.16 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
90.66 MPa

@Strain 0.990 %,
Temperature 40.0 °C
 13150 psi

@Strain 0.990 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
90.94 MPa

@Strain 2.36 %,
Temperature 90.0 °C
 13190 psi

@Strain 2.36 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
93.81 MPa

@Strain 1.61 %,
Temperature 60.0 °C
 13610 psi

@Strain 1.61 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
94.37 MPa

@Strain 3.60 %,
Temperature 120 °C
 13690 psi

@Strain 3.60 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
97.28 MPa

@Strain 4.05 %,
Temperature 120 °C
 14110 psi

@Strain 4.05 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
98.6 MPa

@Strain 4.50 %,
Temperature 120 °C
 14300 psi

@Strain 4.50 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
100.48 MPa

@Strain 2.83 %,
Temperature 90.0 °C
 14573 psi

@Strain 2.83 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
107.82 MPa

@Strain 3.30 %,
Temperature 90.0 °C
 15638 psi

@Strain 3.30 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
108.57 MPa

@Strain 2.00 %,
Temperature 60.0 °C
 15747 psi

@Strain 2.00 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
112.97 MPa

@Strain 3.77 %,
Temperature 90.0 °C
 16385 psi

@Strain 3.77 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
113.41 MPa

@Strain 1.32 %,
Temperature 40.0 °C
 16449 psi

@Strain 1.32 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
115.83 MPa

@Strain 4.24 %,
Temperature 90.0 °C
 16800 psi

@Strain 4.24 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
116.43 MPa

@Strain 1.16 %,
Temperature 0.000 °C
 16887 psi

@Strain 1.16 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
116.5 MPa

@Strain 4.70 %,
Temperature 90.0 °C
 16900 psi

@Strain 4.70 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
121 MPa

@Strain 1.22 %,
Temperature 23.0 °C
 17500 psi

@Strain 1.22 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
121.25 MPa

@Strain 2.41 %,
Temperature 60.0 °C
 17586 psi

@Strain 2.41 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
122.59 MPa

@Strain 1.16 %,
Temperature -20.0 °C
 17780 psi

@Strain 1.16 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
132.27 MPa

@Strain 2.81 %,
Temperature 60.0 °C
 19184 psi

@Strain 2.81 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
133.68 MPa

@Strain 1.66 %,
Temperature 40.0 °C
 19389 psi

@Strain 1.66 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
140.06 MPa

@Strain 3.20 %,
Temperature 60.0 °C
 20314 psi

@Strain 3.20 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
141.3 MPa

@Strain 1.45 %,
Temperature 0.000 °C
 20490 psi

@Strain 1.45 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
144.98 MPa

@Strain 3.61 %,
Temperature 60.0 °C
 21028 psi

@Strain 3.61 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
145.14 MPa

@Strain 1.51 %,
Temperature 23.0 °C
 21051 psi

@Strain 1.51 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
147.5 MPa

@Strain 4.00 %,
Temperature 60.0 °C
 21390 psi

@Strain 4.00 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
148.97 MPa

@Strain 1.46 %,
Temperature -20.0 °C
 21606 psi

@Strain 1.46 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
149.43 MPa

@Strain 1.98 %,
Temperature 40.0 °C
 21673 psi

@Strain 1.98 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
163.24 MPa

@Strain 2.31 %,
Temperature 40.0 °C
 23676 psi

@Strain 2.31 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
164.07 MPa

@Strain 1.74 %,
Temperature 0.000 °C
 23796 psi

@Strain 1.74 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
164.64 MPa

@Strain 1.80 %,
Temperature 23.0 °C
 23879 psi

@Strain 1.80 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
172.5 MPa

@Strain 1.74 %,
Temperature -20.0 °C
 25020 psi

@Strain 1.74 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
174.68 MPa

@Strain 2.65 %,
Temperature 40.0 °C
 25335 psi

@Strain 2.65 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2