DuPont Performance Polymers Zytel® EFE8089B BK416 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® EFE8089B BK416 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® EFE8089B BK416 is a 33% fiber reinforced, heat stabilized, lubricated, toughened polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | DAM; ISO 1183 |
| Filler Content | 33 % | 33 % | DAM |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa @Temperature 23.0 °C |
15100 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 143 MPa @Temperature 23.0 °C |
20700 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 4.5 % @Temperature 23.0 °C |
4.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 8.5 % @Temperature 23.0 °C |
8.5 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 6.00 GPa @Temperature 23.0 °C |
870 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 8.90 GPa @Temperature 23.0 °C |
1290 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 9.80 J/cm² @Temperature 23.0 °C |
46.6 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU |
| 10.3 J/cm² @Temperature 23.0 °C |
49.0 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Glass Fiber Reinforced | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| Toughened Resins | DAM | |
| RoHS Compliance | Contact Manufacturer | DAM |