DuPont Performance Polymers Zytel® HTN 51G15HSL NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 51G15HSL NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G15HSL NC010 is a 15% glass reinforced heat stabilized lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
DAM; ISO 527-1/-2
Tensile Stress 7.27 MPa

@Strain 0.100 %,
Temperature 23.0 °C
1050 psi

@Strain 0.100 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
15.35 MPa

@Strain 0.500 %,
Temperature 150 °C
2226 psi

@Strain 0.500 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
24.36 MPa

@Strain 0.900 %,
Temperature 150 °C
3533 psi

@Strain 0.900 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
30.53 MPa

@Strain 1.30 %,
Temperature 150 °C
4428 psi

@Strain 1.30 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
36.63 MPa

@Strain 0.500 %,
Temperature -40.0 °C
5313 psi

@Strain 0.500 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
39.59 MPa

@Strain 0.600 %,
Temperature 23.0 °C
5742 psi

@Strain 0.600 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
39.81 MPa

@Strain 2.40 %,
Temperature 150 °C
5774 psi

@Strain 2.40 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
57.82 MPa

@Strain 0.900 %,
Temperature 23.0 °C
8386 psi

@Strain 0.900 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
75.35 MPa

@Strain 1.20 %,
Temperature 23.0 °C
10930 psi

@Strain 1.20 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
77.8 MPa

@Strain 1.10 %,
Temperature -40.0 °C
11300 psi

@Strain 1.10 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
97.15 MPa

@Strain 1.40 %,
Temperature -40.0 °C
14090 psi

@Strain 1.40 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
114.97 MPa

@Strain 1.70 %,
Temperature -40.0 °C
16675 psi

@Strain 1.70 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
Elongation at Break 2.1 %
2.1 %
DAM; ISO 527-1/-2
Tensile Modulus 6.50 GPa
943 ksi
DAM; ISO 527-1/-2
Flexural Modulus 5.70 GPa
827 ksi
DAM; ISO 178
Secant Modulus 4.63 GPa

@Strain 2.20 %,
Temperature 100 °C
672 ksi

@Strain 2.20 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
5.12 GPa

@Strain 1.80 %,
Temperature 100 °C
742 ksi

@Strain 1.80 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
5.87 GPa

@Strain 1.20 %,
Temperature 100 °C
851 ksi

@Strain 1.20 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
5.95 GPa

@Strain 1.80 %,
Temperature 23.0 °C
863 ksi

@Strain 1.80 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
6.18 GPa

@Strain 1.40 %,
Temperature 23.0 °C
896 ksi

@Strain 1.40 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
6.32 GPa

@Strain 0.700 %,
Temperature 100 °C
917 ksi

@Strain 0.700 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
6.378 GPa

@Strain 1.00 %,
Temperature 23.0 °C
925.1 ksi

@Strain 1.00 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
6.56 GPa

@Strain 1.90 %,
Temperature -40.0 °C
951 ksi

@Strain 1.90 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
6.60 GPa

@Strain 0.600 %,
Temperature 23.0 °C
957 ksi

@Strain 0.600 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
6.665 GPa

@Strain 0.200 %,
Temperature 100 °C
966.7 ksi

@Strain 0.200 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
6.89 GPa

@Strain 1.50 %,
Temperature -40.0 °C
999 ksi

@Strain 1.50 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
7.07 GPa

@Strain 1.10 %,
Temperature -40.0 °C
1030 ksi

@Strain 1.10 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
7.27 GPa

@Strain 0.100 %,
Temperature 23.0 °C
1050 ksi

@Strain 0.100 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
7.326 GPa

@Strain 0.500 %,
Temperature -40.0 °C
1063 ksi

@Strain 0.500 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
DAM; ISO 180/1A
6.00 kJ/m²

@Temperature -40.0 °C
2.86 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 180/1A
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
DAM; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
DAM; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
DAM; ISO 11359-1/-2
57.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 64.0 µm/m-°C
35.6 µin/in-°F
DAM; ISO 11359-1/-2
30.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
77.0 µm/m-°C

@Temperature 55.0 - 160 °C
42.8 µin/in-°F

@Temperature 131 - 320 °F
DAM; ISO 11359-1/-2
Melting Point 300 °C
572 °F
DAM; first heat; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 276 °C
529 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 254 °C
489 °F
DAM; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
DAM; IEC 60695-11-10
Oxygen Index 23 %
23 %
DAM; ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
DAM; IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
50%RH; IEC 60093
Comparative Tracking Index 600 V
600 V
DAM; IEC 60112
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >PA6T/XT-GF15<
ISO 11469
>PPA-GF15<
SAE J1344
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Special Characteristics Heat stabilised or stable to heat
UL recognition UL
DAM