DuPont Performance Polymers Zytel® HTN 51G35HSL BK083 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 51G35HSL BK083 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G35HSL BK083 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
50%RH; ISO 527-1/-2
210 MPa
30500 psi
DAM; ISO 527-1/-2
Tensile Stress 8.88 MPa

@Strain 0.190 %,
Temperature 150 °C
1290 psi

@Strain 0.190 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
12.91 MPa

@Strain 0.280 %,
Temperature 180 °C
1872 psi

@Strain 0.280 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
20.41 MPa

@Strain 0.360 %,
Temperature 150 °C
2960 psi

@Strain 0.360 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
24.59 MPa

@Strain 0.650 %,
Temperature 150 °C
3566 psi

@Strain 0.650 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
38.11 MPa

@Strain 1.15 %,
Temperature 180 °C
5527 psi

@Strain 1.15 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
38.35 MPa

@Strain 1.40 %,
Temperature 150 °C
5562 psi

@Strain 1.40 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
40.83 MPa

@Strain 0.550 %,
Temperature 90.0 °C
5922 psi

@Strain 0.550 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
46.25 MPa

@Strain 2.23 %,
Temperature 150 °C
6708 psi

@Strain 2.23 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
48.71 MPa

@Strain 1.24 %,
Temperature 150 °C
7065 psi

@Strain 1.24 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
48.84 MPa

@Strain 2.11 %,
Temperature 180 °C
7084 psi

@Strain 2.11 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
55.6 MPa

@Strain 3.25 %,
Temperature 180 °C
8060 psi

@Strain 3.25 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
60.42 MPa

@Strain 2.38 %,
Temperature 150 °C
8763 psi

@Strain 2.38 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
65.19 MPa

@Strain 0.600 %,
Temperature 90.0 °C
9455 psi

@Strain 0.600 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
66.06 MPa

@Strain 1.14 %,
Temperature 90.0 °C
9581 psi

@Strain 1.14 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
66.18 MPa

@Strain 3.75 %,
Temperature 150 °C
9599 psi

@Strain 3.75 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
73.19 MPa

@Strain 0.620 %,
Temperature 40.0 °C
10620 psi

@Strain 0.620 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
80.45 MPa

@Strain 1.80 %,
Temperature 90.0 °C
11670 psi

@Strain 1.80 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
83.19 MPa

@Strain 0.720 %,
Temperature 23.0 °C
12070 psi

@Strain 0.720 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
88.89 MPa

@Strain 2.62 %,
Temperature 90.0 °C
12890 psi

@Strain 2.62 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
91.36 MPa

@Strain 0.760 %,
Temperature 23.0 °C
13250 psi

@Strain 0.760 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
97.16 MPa

@Strain 0.780 %,
Temperature -20.0 °C
14090 psi

@Strain 0.780 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
98.0 MPa

@Strain 0.897 %,
Temperature 40.0 °C
14200 psi

@Strain 0.897 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
98.97 MPa

@Strain 0.800 %,
Temperature 0.000 °C
14350 psi

@Strain 0.800 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
102.66 MPa

@Strain 1.02 %,
Temperature 90.0 °C
14890 psi

@Strain 1.02 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
104.24 MPa

@Strain 0.910 %,
Temperature 40.0 °C
15119 psi

@Strain 0.910 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
107 MPa

@Strain 0.882 %,
Temperature 0.000 °C
15500 psi

@Strain 0.882 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
112.48 MPa

@Strain 1.02 %,
Temperature 23.0 °C
16314 psi

@Strain 1.02 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
116.13 MPa

@Strain 0.930 %,
Temperature -20.0 °C
16843 psi

@Strain 0.930 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
125.83 MPa

@Strain 1.36 %,
Temperature 90.0 °C
18250 psi

@Strain 1.36 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
131.27 MPa

@Strain 1.30 %,
Temperature 40.0 °C
19039 psi

@Strain 1.30 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
134.89 MPa

@Strain 1.14 %,
Temperature 0.000 °C
19564 psi

@Strain 1.14 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
137.92 MPa

@Strain 1.31 %,
Temperature 23.0 °C
20004 psi

@Strain 1.31 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
146.77 MPa

@Strain 1.80 %,
Temperature 90.0 °C
21287 psi

@Strain 1.80 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
153.67 MPa

@Strain 1.28 %,
Temperature -20.0 °C
22288 psi

@Strain 1.28 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
156.27 MPa

@Strain 1.48 %,
Temperature 40.0 °C
22665 psi

@Strain 1.48 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
156.32 MPa

@Strain 1.66 %,
Temperature 40.0 °C
22672 psi

@Strain 1.66 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
159.92 MPa

@Strain 1.46 %,
Temperature 23.0 °C
23194 psi

@Strain 1.46 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
162.15 MPa

@Strain 1.62 %,
Temperature 23.0 °C
23518 psi

@Strain 1.62 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
177.86 MPa

@Strain 2.09 %,
Temperature 40.0 °C
25796 psi

@Strain 2.09 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
181.2 MPa

@Strain 1.65 %,
Temperature 0.000 °C
26280 psi

@Strain 1.65 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
187.3 MPa

@Strain 1.72 %,
Temperature 0.000 °C
27170 psi

@Strain 1.72 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
189.71 MPa

@Strain 1.97 %,
Temperature 40.0 °C
27515 psi

@Strain 1.97 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
191.21 MPa

@Strain 1.74 %,
Temperature -20.0 °C
27733 psi

@Strain 1.74 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
204.28 MPa

@Strain 1.96 %,
Temperature 0.000 °C
29628 psi

@Strain 1.96 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
205.31 MPa

@Strain 2.10 %,
Temperature 23.0 °C
29778 psi

@Strain 2.10 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
210.24 MPa

@Strain 2.06 %,
Temperature 0.000 °C
30493 psi

@Strain 2.06 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
216.76 MPa

@Strain 2.02 %,
Temperature -20.0 °C
31438 psi

@Strain 2.02 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
Elongation at Break 2.3 %
2.3 %
50%RH; ISO 527-1/-2
2.4 %
2.4 %
DAM; ISO 527-1/-2
Tensile Modulus 11.5 GPa
1670 ksi
50%RH; ISO 527-1/-2
12.0 GPa
1740 ksi
DAM; ISO 527-1/-2
Flexural Modulus 10.0 GPa
1450 ksi
50%RH; ISO 178
10.5 GPa
1520 ksi
DAM; ISO 178
Secant Modulus 1.01 GPa

@Strain 5.47 %,
Temperature 200 °C
147 ksi

@Strain 5.47 %,
Temperature 392 °F
DAM; ISO 11403-1 -2
1.29 GPa

@Strain 4.02 %,
Temperature 200 °C
187 ksi

@Strain 4.02 %,
Temperature 392 °F
DAM; ISO 11403-1 -2
1.75 GPa

@Strain 2.63 %,
Temperature 200 °C
254 ksi

@Strain 2.63 %,
Temperature 392 °F
DAM; ISO 11403-1 -2
2.71 GPa

@Strain 1.30 %,
Temperature 200 °C
393 ksi

@Strain 1.30 %,
Temperature 392 °F
DAM; ISO 11403-1 -2
4.2425 GPa

@Strain 0.400 %,
Temperature 200 °C
615.33 ksi

@Strain 0.400 %,
Temperature 392 °F
DAM; ISO 11403-1 -2
7.40 GPa

@Strain 2.54 %,
Temperature 40.0 °C
1070 ksi

@Strain 2.54 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
8.70 GPa

@Strain 2.33 %,
Temperature 23.0 °C
1260 ksi

@Strain 2.33 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2