DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G35HSLR BK420 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin with improved hydrolysis resistance. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 310 MPa
45000 psi
DAM; H 961/30; ISO 2039-1
Tensile Strength at Break 190 MPa
27600 psi
50%RH; ISO 527-1/-2
200 MPa
29000 psi
DAM; ISO 527-1/-2
Tensile Stress 11.35 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1646 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
17.63 MPa

@Strain 0.300 %,
Temperature 150 °C
 2557 psi

@Strain 0.300 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
43.48 MPa

@Strain 0.800 %,
Temperature 150 °C
 6306 psi

@Strain 0.800 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
54.0 MPa

@Strain 1.10 %,
Temperature 150 °C
 7830 psi

@Strain 1.10 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
64.12 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 9300 psi

@Strain 0.500 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
65.54 MPa

@Strain 1.60 %,
Temperature 150 °C
 9506 psi

@Strain 1.60 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
66.07 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 9583 psi

@Strain 0.600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
96.19 MPa

@Strain 0.900 %,
Temperature 23.0 °C
 13950 psi

@Strain 0.900 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
96.76 MPa

@Strain 0.800 %,
Temperature -40.0 °C
 14030 psi

@Strain 0.800 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
130.11 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 18871 psi

@Strain 1.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
144.37 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 20939 psi

@Strain 1.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
176.86 MPa

@Strain 1.70 %,
Temperature -40.0 °C
 25651 psi

@Strain 1.70 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
190.97 MPa

@Strain 2.30 %,
Temperature 23.0 °C
 27698 psi

@Strain 2.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
50%RH; ISO 527-1/-2
2.3 %
2.3 %
DAM; ISO 527-1/-2
Tensile Modulus 11.5 GPa
1670 ksi
DAM; ISO 527-1/-2
11.5 GPa
1670 ksi
50%RH; ISO 527-1/-2
Flexural Modulus 10.5 GPa
1520 ksi
DAM; ISO 178
Secant Modulus 6.36 GPa

@Strain 2.30 %,
Temperature 100 °C
 923 ksi

@Strain 2.30 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
7.10 GPa

@Strain 1.90 %,
Temperature 100 °C
 1030 ksi

@Strain 1.90 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
7.774 GPa

@Strain 1.50 %,
Temperature 100 °C
 1128 ksi

@Strain 1.50 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
8.387 GPa

@Strain 1.00 %,
Temperature 100 °C
 1216 ksi

@Strain 1.00 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
8.64 GPa

@Strain 0.300 %,
Temperature 100 °C
 1250 ksi

@Strain 0.300 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
8.833 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 1281 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
9.2125 GPa

@Strain 2.40 %,
Temperature -40.0 °C
 1336.2 ksi

@Strain 2.40 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
9.67 GPa

@Strain 1.50 %,
Temperature 23.0 °C
 1400 ksi

@Strain 1.50 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
9.898 GPa

@Strain 2.00 %,
Temperature -40.0 °C
 1436 ksi

@Strain 2.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
10.527 GPa

@Strain 1.00 %,
Temperature 23.0 °C
 1526.8 ksi

@Strain 1.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
10.9 GPa

@Strain 1.40 %,
Temperature -40.0 °C
 1580 ksi

@Strain 1.40 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
11.0 GPa

@Strain 0.600 %,
Temperature 23.0 °C
 1600 ksi

@Strain 0.600 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
11.35 GPa

@Strain 0.100 %,
Temperature 23.0 °C
 1646 ksi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
12.095 GPa

@Strain 0.800 %,
Temperature -40.0 °C
 1754.3 ksi

@Strain 0.800 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
12.824 GPa

@Strain 0.500 %,
Temperature -40.0 °C
 1860.0 ksi

@Strain 0.500 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
50%RH; ISO 179/1eU
5.00 J/cm²
23.8 ft-lb/in²
DAM; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
50%RH; ISO 179/1eA
0.900 J/cm²
4.28 ft-lb/in²
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
DAM; ISO 11359-1/-2
20.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 11.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 58.0 µm/m-°C
32.2 µin/in-°F
DAM; ISO 11359-1/-2
55.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
Melting Point 300 °C
572 °F
DAM; first heat; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 276 °C
529 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
DAM; ISO 75-1/-2
Flame Spread 28 mm/min

@Thickness 1.00 mm
 1.1 in/min

@Thickness 0.0394 in
 ISO 3795 (FMVSS 302)
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
DAM; IEC 60093
Dielectric Strength 33.0 kV/mm
838 kV/in
50%RH; IEC 60243-1
34.0 kV/mm
864 kV/in
DAM; IEC 60243-1
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >PA6T/XT-GF35<
ISO 11469
>PPA-GF35<
SAE J1344
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Special Characteristics Heat stabilised or stable to heat
Users viewing this material also viewed the following: