DuPont Performance Polymers Zytel® HTN 54G35HSLR BK031 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 54G35HSLR BK031 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced Toughened PPA High Performance Polyamide Zytel HTN54G35HSLR BK031 is a 35% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 166 MPa
24100 psi
50%RH; ISO 527-1/-2
180 MPa
26100 psi
DAM; ISO 527-1/-2
Tensile Stress 8.18 MPa

@Strain 0.200 %,
Temperature 160 °C
 1190 psi

@Strain 0.200 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
10.34 MPa

@Strain 0.240 %,
Temperature 150 °C
 1500 psi

@Strain 0.240 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
10.35 MPa

@Strain 0.280 %,
Temperature 180 °C
 1501 psi

@Strain 0.280 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
19.46 MPa

@Strain 0.660 %,
Temperature 150 °C
 2822 psi

@Strain 0.660 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
23.18 MPa

@Strain 0.510 %,
Temperature 90.0 °C
 3362 psi

@Strain 0.510 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
34.46 MPa

@Strain 1.68 %,
Temperature 180 °C
 4998 psi

@Strain 1.68 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
35.54 MPa

@Strain 1.88 %,
Temperature 150 °C
 5155 psi

@Strain 1.88 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
38.47 MPa

@Strain 0.410 %,
Temperature 40.0 °C
 5580 psi

@Strain 0.410 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
38.99 MPa

@Strain 1.46 %,
Temperature 150 °C
 5655 psi

@Strain 1.46 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
41.77 MPa

@Strain 0.420 %,
Temperature 23.0 °C
 6058 psi

@Strain 0.420 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
42.56 MPa

@Strain 2.96 %,
Temperature 150 °C
 6173 psi

@Strain 2.96 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
42.6 MPa

@Strain 2.83 %,
Temperature 180 °C
 6180 psi

@Strain 2.83 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
43.27 MPa

@Strain 2.12 %,
Temperature 160 °C
 6276 psi

@Strain 2.12 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
46.19 MPa

@Strain 0.520 %,
Temperature 90.0 °C
 6699 psi

@Strain 0.520 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
46.8 MPa

@Strain 1.48 %,
Temperature 90.0 °C
 6790 psi

@Strain 1.48 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
47.43 MPa

@Strain 4.18 %,
Temperature 150 °C
 6879 psi

@Strain 4.18 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
48.05 MPa

@Strain 4.06 %,
Temperature 180 °C
 6969 psi

@Strain 4.06 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
49.84 MPa

@Strain 2.55 %,
Temperature 150 °C
 7229 psi

@Strain 2.55 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
50.98 MPa

@Strain 3.26 %,
Temperature 160 °C
 7394 psi

@Strain 3.26 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
53.25 MPa

@Strain 0.530 %,
Temperature 0.000 °C
 7723 psi

@Strain 0.530 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
56.27 MPa

@Strain 4.49 %,
Temperature 160 °C
 8161 psi

@Strain 4.49 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
56.53 MPa

@Strain 8.18 %,
Temperature 180 °C
 8199 psi

@Strain 8.18 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
56.83 MPa

@Strain 3.74 %,
Temperature 150 °C
 8243 psi

@Strain 3.74 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
57.85 MPa

@Strain 2.41 %,
Temperature 90.0 °C
 8390 psi

@Strain 2.41 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
64.81 MPa

@Strain 3.58 %,
Temperature 90.0 °C
 9400 psi

@Strain 3.58 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
71.62 MPa

@Strain 0.840 %,
Temperature 40.0 °C
 10390 psi

@Strain 0.840 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
73.53 MPa

@Strain 0.700 %,
Temperature -20.0 °C
 10660 psi

@Strain 0.700 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
74.28 MPa

@Strain 0.920 %,
Temperature 90.0 °C
 10770 psi

@Strain 0.920 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
92.13 MPa

@Strain 0.950 %,
Temperature 0.000 °C
 13360 psi

@Strain 0.950 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
93.07 MPa

@Strain 1.19 %,
Temperature 40.0 °C
 13500 psi

@Strain 1.19 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
96.7 MPa

@Strain 0.990 %,
Temperature 23.0 °C
 14000 psi

@Strain 0.990 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
97.7 MPa

@Strain 1.38 %,
Temperature 90.0 °C
 14200 psi

@Strain 1.38 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
105.87 MPa

@Strain 1.13 %,
Temperature 40.0 °C
 15355 psi

@Strain 1.13 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
113.12 MPa

@Strain 1.64 %,
Temperature 40.0 °C
 16407 psi

@Strain 1.64 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
113.98 MPa

@Strain 1.92 %,
Temperature 90.0 °C
 16531 psi

@Strain 1.92 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
117.77 MPa

@Strain 1.19 %,
Temperature 0.000 °C
 17081 psi

@Strain 1.19 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
119.44 MPa

@Strain 1.28 %,
Temperature 0.000 °C
 17323 psi

@Strain 1.28 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
123 MPa

@Strain 1.24 %,
Temperature -20.0 °C
 17800 psi

@Strain 1.24 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
126.69 MPa

@Strain 1.58 %,
Temperature 23.0 °C
 18375 psi

@Strain 1.58 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
129.67 MPa

@Strain 1.41 %,
Temperature 23.0 °C
 18807 psi

@Strain 1.41 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
144.07 MPa

@Strain 1.65 %,
Temperature 0.000 °C
 20896 psi

@Strain 1.65 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
146.8 MPa

@Strain 2.07 %,
Temperature 23.0 °C
 21290 psi

@Strain 2.07 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
149.32 MPa

@Strain 1.84 %,
Temperature 40.0 °C
 21657 psi

@Strain 1.84 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
154.64 MPa

@Strain 1.66 %,
Temperature 0.000 °C
 22429 psi

@Strain 1.66 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
154.84 MPa

@Strain 1.82 %,
Temperature 23.0 °C
 22458 psi

@Strain 1.82 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
160.4 MPa

@Strain 2.83 %,
Temperature 23.0 °C
 23260 psi

@Strain 2.83 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
167.73 MPa

@Strain 1.81 %,
Temperature -20.0 °C
 24327 psi

@Strain 1.81 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
168.89 MPa

@Strain 2.36 %,
Temperature 40.0 °C
 24495 psi

@Strain 2.36 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
176.66 MPa

@Strain 2.29 %,
Temperature 23.0 °C
 25622 psi

@Strain 2.29 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
180.28 MPa

@Strain 3.17 %,
Temperature 40.0 °C
 26147 psi

@Strain 3.17 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
183.66 MPa

@Strain 2.16 %,
Temperature 0.000 °C
 26638 psi

@Strain 2.16 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
189.09 MPa

@Strain 2.22 %,
Temperature -20.0 °C
 27425 psi

@Strain 2.22 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
196.56 MPa

@Strain 2.28 %,
Temperature -20.0 °C
 28509 psi

@Strain 2.28 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
206.46 MPa

@Strain 2.72 %,
Temperature 0.000 °C
 29945 psi

@Strain 2.72 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
211.27 MPa

@Strain 2.82 %,
Temperature -20.0 °C
 30642 psi

@Strain 2.82 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
222.55 MPa

@Strain 2.86 %,
Temperature -20.0 °C
 32278 psi

@Strain 2.86 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.7 %
2.7 %
50%RH; ISO 527-1/-2
3.0 %
3.0 %
DAM; ISO 527-1/-2
Tensile Modulus 10.5 GPa
1520 ksi
DAM; ISO 527-1/-2
10.8 GPa
1570 ksi
50%RH; ISO 527-1/-2