DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® HTN54G35HSLR NC010 is a 35% glass reinforced, toughened, heat stabilized, lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
DAM; ISO 1183
Filler Content 35 %
35 %
DAM
Water Absorption 0.64 %

@Temperature 23.0 °C
0.64 %

@Temperature 73.4 °F
Immersion 24h; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
0.0020 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Thickness 2.00 mm
0.0060 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Melt Index of Compound 5.5 g/10 min

@Load 2.16 kg,
Temperature 325 °C
5.5 g/10 min

@Load 4.76 lb,
Temperature 617 °F
DAM; cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 180 MPa

@Temperature 23.0 °C
26100 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 2.7 %

@Temperature 23.0 °C
2.7 %

@Temperature 73.4 °F
50%RH; ISO 527
3.0 %

@Temperature 23.0 °C
3.0 %

@Temperature 73.4 °F
DAM; ISO 527
Tensile Modulus 10.0 GPa

@Temperature 23.0 °C
1450 ksi

@Temperature 73.4 °F
DAM; ISO 527
11.0 GPa

@Temperature 23.0 °C
1600 ksi

@Temperature 73.4 °F
50%RH; ISO 527
Flexural Modulus 9.00 GPa

@Temperature 23.0 °C
1310 ksi

@Temperature 73.4 °F
DAM; ISO 178
Charpy Impact Unnotched 7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -40.0 °C
4.28 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 179/1eA
1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 11000 MPa

@Temperature 23.0 °C
1.60e+6 psi

@Temperature 73.4 °F
50%RH; ISO 899
Tensile Creep Modulus, 1000 hours 10000 MPa

@Temperature 23.0 °C
1.45e+6 psi

@Temperature 73.4 °F
50%RH; ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
500 µm/m-°C

@Temperature 130 - 200 °C
278 µin/in-°F

@Temperature 266 - 392 °F
DAM; ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
40.0 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
75.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
100 µm/m-°C

@Temperature 130 - 200 °C
55.6 µin/in-°F

@Temperature 266 - 392 °F
DAM; ISO 11359-1/-2
Melting Point 300 °C
572 °F
10°C/min, First Heat; DAM; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 285 °C
545 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
DAM; ISO 75-1/-2
Electrical Properties Metric English Comments
Surface Resistance 1.00e+14 ohm

@Temperature 23.0 °C
1.00e+14 ohm

@Temperature 73.4 °F
50%RH; IEC 60093
Comparative Tracking Index 600 V

@Temperature 23.0 °C
600 V

@Temperature 73.4 °F
DAM; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 325 °C
617 °F
DAM; Optimum
320 - 330 °C
608 - 626 °F
DAM
Mold Temperature 95.0 °C
203 °F
DAM; optimum
85.0 - 135 °C
185 - 275 °F
DAM
Drying Temperature 100 °C
212 °F
DAM
Dry Time 6.00 - 8.00 hour
6.00 - 8.00 hour
DAM
Moisture Content <= 0.10 %
<= 0.10 %
DAM
Descriptive Properties Value Comments
Appearance Natural Color
DAM
Features Hydrolysis Resistant
DAM
Filler Glass Fiber reinforcement
DAM
Forms Pellets
DAM
Generic Polyphthalamide (PPA)
DAM
Material Status Current
DAM
Part Marking Code >PA-IGF35<
ISO 11469; DAM
>PPA-IGF35<
SAE J1344; DAM
Polymer Family High performance polyamide
DAM
Polymer Type Partially Aromatic PA, PPA
DAM
Processing Method Injection Molding
DAM
Product Category Glass Reinforced Resins
DAM
Hydrolysis Resistant Resins
DAM
Toughened Resins
DAM
Region Available - Global Yes
DAM
Resin Identification PA6T/XT+PA6T/66-IGF35
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM