DuPont Performance Polymers Zytel® HTN FR52G20NH NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FR52G20NH NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G20NH NC010 is a 20% glass reinforced flame retardant lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated flaInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
50%RH; ISO 527-1/-2
135 MPa
19600 psi
DAM; ISO 527-1/-2
Tensile Stress 4.29 MPa

@Strain 0.100 %,
Temperature 150 °C
622 psi

@Strain 0.100 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
4.34 MPa

@Strain 0.100 %,
Temperature 150 °C
629 psi

@Strain 0.100 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
8.65 MPa

@Strain 0.100 %,
Temperature 40.0 °C
1250 psi

@Strain 0.100 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
8.95 MPa

@Strain 0.100 %,
Temperature 40.0 °C
1300 psi

@Strain 0.100 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
9.02 MPa

@Strain 0.100 %,
Temperature -40.0 °C
1310 psi

@Strain 0.100 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
9.15 MPa

@Strain 0.100 %,
Temperature 23.0 °C
1330 psi

@Strain 0.100 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
9.22 MPa

@Strain 0.100 %,
Temperature 23.0 °C
1340 psi

@Strain 0.100 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
10.24 MPa

@Strain 0.100 %,
Temperature -40.0 °C
1485 psi

@Strain 0.100 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
15.28 MPa

@Strain 0.400 %,
Temperature 150 °C
2216 psi

@Strain 0.400 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
15.8 MPa

@Strain 0.400 %,
Temperature 150 °C
2290 psi

@Strain 0.400 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
24.44 MPa

@Strain 0.700 %,
Temperature 150 °C
3545 psi

@Strain 0.700 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
24.97 MPa

@Strain 0.700 %,
Temperature 150 °C
3622 psi

@Strain 0.700 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
31.73 MPa

@Strain 0.400 %,
Temperature 40.0 °C
4602 psi

@Strain 0.400 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
31.91 MPa

@Strain 1.00 %,
Temperature 150 °C
4628 psi

@Strain 1.00 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
32.5 MPa

@Strain 1.00 %,
Temperature 150 °C
4710 psi

@Strain 1.00 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
33.65 MPa

@Strain 0.400 %,
Temperature 40.0 °C
4881 psi

@Strain 0.400 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
33.98 MPa

@Strain 0.400 %,
Temperature -40.0 °C
4928 psi

@Strain 0.400 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
34.51 MPa

@Strain 0.400 %,
Temperature 23.0 °C
5005 psi

@Strain 0.400 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
34.75 MPa

@Strain 0.400 %,
Temperature 23.0 °C
5040 psi

@Strain 0.400 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
38.69 MPa

@Strain 0.400 %,
Temperature -40.0 °C
5612 psi

@Strain 0.400 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
47.07 MPa

@Strain 1.90 %,
Temperature 150 °C
6827 psi

@Strain 1.90 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
48.61 MPa

@Strain 1.90 %,
Temperature 150 °C
7050 psi

@Strain 1.90 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
51.63 MPa

@Strain 2.40 %,
Temperature 150 °C
7488 psi

@Strain 2.40 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
51.88 MPa

@Strain 0.700 %,
Temperature 40.0 °C
7525 psi

@Strain 0.700 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
54.51 MPa

@Strain 3.00 %,
Temperature 150 °C
7906 psi

@Strain 3.00 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
54.56 MPa

@Strain 2.40 %,
Temperature 150 °C
7913 psi

@Strain 2.40 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
54.79 MPa

@Strain 0.700 %,
Temperature 40.0 °C
7947 psi

@Strain 0.700 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
55.59 MPa

@Strain 3.40 %,
Temperature 150 °C
8063 psi

@Strain 3.40 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
56.37 MPa

@Strain 0.700 %,
Temperature 23.0 °C
8176 psi

@Strain 0.700 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
56.42 MPa

@Strain 3.90 %,
Temperature 150 °C
8183 psi

@Strain 3.90 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
56.61 MPa

@Strain 0.700 %,
Temperature 23.0 °C
8211 psi

@Strain 0.700 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
57.07 MPa

@Strain 4.70 %,
Temperature 150 °C
8277 psi

@Strain 4.70 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
57.08 MPa

@Strain 4.80 %,
Temperature 150 °C
8279 psi

@Strain 4.80 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
57.23 MPa

@Strain 0.700 %,
Temperature -40.0 °C
8301 psi

@Strain 0.700 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
58.99 MPa

@Strain 3.00 %,
Temperature 150 °C
8556 psi

@Strain 3.00 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
60.71 MPa

@Strain 3.40 %,
Temperature 150 °C
8805 psi

@Strain 3.40 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
62.07 MPa

@Strain 3.90 %,
Temperature 150 °C
9003 psi

@Strain 3.90 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
63.26 MPa

@Strain 4.70 %,
Temperature 150 °C
9175 psi

@Strain 4.70 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
63.36 MPa

@Strain 4.80 %,
Temperature 150 °C
9190 psi

@Strain 4.80 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
63.85 MPa

@Strain 0.700 %,
Temperature -40.0 °C
9261 psi

@Strain 0.700 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
68.6 MPa

@Strain 1.00 %,
Temperature 40.0 °C
9950 psi

@Strain 1.00 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
73.39 MPa

@Strain 1.00 %,
Temperature 40.0 °C
10640 psi

@Strain 1.00 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
74.94 MPa

@Strain 1.00 %,
Temperature 23.0 °C
10870 psi

@Strain 1.00 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
75.79 MPa

@Strain 1.00 %,
Temperature 23.0 °C
10990 psi

@Strain 1.00 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
78.11 MPa

@Strain 1.00 %,
Temperature -40.0 °C
11330 psi

@Strain 1.00 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
86.01 MPa

@Strain 1.00 %,
Temperature -40.0 °C
12470 psi

@Strain 1.00 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
102.8 MPa

@Strain 1.90 %,
Temperature 40.0 °C
14910 psi

@Strain 1.90 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
113.44 MPa

@Strain 1.90 %,
Temperature 23.0 °C
16453 psi

@Strain 1.90 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
116.15 MPa

@Strain 1.90 %,
Temperature 40.0 °C
16846 psi

@Strain 1.90 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
120.9 MPa

@Strain 1.90 %,
Temperature 23.0 °C
17540 psi

@Strain 1.90 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
129.83 MPa

@Strain 1.90 %,
Temperature -40.0 °C
18830 psi

@Strain 1.90 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
130.27 MPa

@Strain 2.40 %,
Temperature 40.0 °C
18894 psi

@Strain 2.40 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
137.15 MPa

@Strain 2.40 %,
Temperature 23.0 °C
19892 psi

@Strain 2.40 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
139.65 MPa

@Strain 1.90 %,
Temperature -40.0 °C
20255 psi

@Strain 1.90 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
152.75 MPa

@Strain 2.40 %,
Temperature -40.0 °C
22155 psi

@Strain 2.40 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
Elongation at Break 2.2 %
2.2 %
50%RH; ISO 527-1/-2
2.4 %
2.4 %
DAM; ISO 527-1/-2
Tensile Modulus 8.20 GPa
1190 ksi
DAM; ISO 527-1/-2
8.60 GPa
1250 ksi
50%RH; ISO 527-1/-2
Flexural Strength 180 MPa
26100 psi
50%RH; ISO 178