DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel® PLUS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® PLS93G35DH1 BK261 is a 35% glass reinforced PA6 using SHIELD Technology, only from DuPont, it provides exceptional welding resistance & retention over time thanks to excellent Heat Resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
DAM; ISO 1183
Filler Content 35 %
35 %
DAM
Water Absorption 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
 0.0020 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 2.00 mm
 0.0070 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
 50%RH; ISO 527
197 MPa

@Temperature 23.0 °C
 28600 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 0.510 MPa

@Strain 0.000 %,
Temperature 200 °C
 74.0 psi

@Strain 0.000 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
0.830 MPa

@Strain 0.000 %,
Temperature 180 °C
 120 psi

@Strain 0.000 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
0.880 MPa

@Strain 0.000 %,
Temperature 150 °C
 128 psi

@Strain 0.000 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
0.910 MPa

@Strain 0.000 %,
Temperature 150 °C
 132 psi

@Strain 0.000 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
0.950 MPa

@Strain 0.000 %,
Temperature 120 °C
 138 psi

@Strain 0.000 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
1.09 MPa

@Strain 0.000 %,
Temperature 120 °C
 158 psi

@Strain 0.000 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
1.09 MPa

@Strain 0.000 %,
Temperature 90.0 °C
 158 psi

@Strain 0.000 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
1.17 MPa

@Strain 0.000 %,
Temperature 90.0 °C
 170 psi

@Strain 0.000 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
1.19 MPa

@Strain 0.000 %,
Temperature 60.0 °C
 173 psi

@Strain 0.000 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
1.23 MPa

@Strain 0.000 %,
Temperature 40.0 °C
 178 psi

@Strain 0.000 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
1.28 MPa

@Strain 0.000 %,
Temperature 23.0 °C
 186 psi

@Strain 0.000 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
1.34 MPa

@Strain 0.000 %,
Temperature 0.000 °C
 194 psi

@Strain 0.000 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
1.38 MPa

@Strain 0.000 %,
Temperature 60.0 °C
 200 psi

@Strain 0.000 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
1.56 MPa

@Strain 0.000 %,
Temperature 0.000 °C
 226 psi

@Strain 0.000 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
1.81 MPa

@Strain 0.000 %,
Temperature 40.0 °C
 263 psi

@Strain 0.000 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
1.92 MPa

@Strain 0.000 %,
Temperature -20.0 °C
 278 psi

@Strain 0.000 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
1.95 MPa

@Strain 0.000 %,
Temperature -20.0 °C
 283 psi

@Strain 0.000 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
1.98 MPa

@Strain 0.000 %,
Temperature 23.0 °C
 287 psi

@Strain 0.000 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
2.76 MPa

@Strain 0.0400 %,
Temperature -20.0 °C
 400 psi

@Strain 0.0400 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
2.90 MPa

@Strain 0.100 %,
Temperature 200 °C
 421 psi

@Strain 0.100 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
2.94 MPa

@Strain 0.0600 %,
Temperature 150 °C
 426 psi

@Strain 0.0600 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
3.19 MPa

@Strain 0.0600 %,
Temperature 180 °C
 463 psi

@Strain 0.0600 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
3.32 MPa

@Strain 0.0600 %,
Temperature 120 °C
 482 psi

@Strain 0.0600 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
3.75 MPa

@Strain 0.0200 %,
Temperature -20.0 °C
 544 psi

@Strain 0.0200 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2
3.90 MPa

@Strain 0.0700 %,
Temperature 150 °C
 566 psi

@Strain 0.0700 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
3.92 MPa

@Strain 0.0500 %,
Temperature 90.0 °C
 569 psi

@Strain 0.0500 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
4.40 MPa

@Strain 0.0600 %,
Temperature 60.0 °C
 638 psi

@Strain 0.0600 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
4.42 MPa

@Strain 0.0700 %,
Temperature 120 °C
 641 psi

@Strain 0.0700 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
4.70 MPa

@Strain 0.0600 %,
Temperature 40.0 °C
 682 psi

@Strain 0.0600 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
4.86 MPa

@Strain 0.0800 %,
Temperature 90.0 °C
 705 psi

@Strain 0.0800 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
4.88 MPa

@Strain 0.190 %,
Temperature 200 °C
 708 psi

@Strain 0.190 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
4.95 MPa

@Strain 0.110 %,
Temperature 150 °C
 718 psi

@Strain 0.110 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
5.23 MPa

@Strain 0.0500 %,
Temperature 23.0 °C
 759 psi

@Strain 0.0500 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
5.52 MPa

@Strain 0.0700 %,
Temperature 60.0 °C
 801 psi

@Strain 0.0700 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
5.54 MPa

@Strain 0.140 %,
Temperature 180 °C
 804 psi

@Strain 0.140 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
5.69 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
 825 psi

@Strain 0.0500 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
5.70 MPa

@Strain 0.120 %,
Temperature 120 °C
 827 psi

@Strain 0.120 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
5.99 MPa

@Strain 0.0500 %,
Temperature 40.0 °C
 869 psi

@Strain 0.0500 %,
Temperature 104 °F
 DAM; ISO 11403-1/-2
6.51 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
 944 psi

@Strain 0.0400 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
6.60 MPa

@Strain 0.120 %,
Temperature 90.0 °C
 957 psi

@Strain 0.120 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
6.76 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
 980 psi

@Strain 0.0500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1/-2
6.90 MPa

@Strain 0.170 %,
Temperature 150 °C
 1000 psi

@Strain 0.170 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
6.94 MPa

@Strain 0.150 %,
Temperature 150 °C
 1010 psi

@Strain 0.150 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
7.54 MPa

@Strain 0.0900 %,
Temperature -20.0 °C
 1090 psi

@Strain 0.0900 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
7.63 MPa

@Strain 0.110 %,
Temperature 60.0 °C
 1110 psi

@Strain 0.110 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
7.69 MPa

@Strain 0.200 %,
Temperature 180 °C
 1120 psi

@Strain 0.200 %,
Temperature 356 °F
 DAM; ISO 11403-1/-2
7.75 MPa

@Strain 0.150 %,
Temperature 120 °C
 1120 psi

@Strain 0.150 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
7.91 MPa

@Strain 0.180 %,
Temperature 120 °C
 1150 psi

@Strain 0.180 %,
Temperature 248 °F
 50%RH; ISO 11403-1/-2
8.13 MPa

@Strain 0.110 %,
Temperature 40.0 °C
 1180 psi

@Strain 0.110 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
8.56 MPa

@Strain 0.150 %,
Temperature 90.0 °C
 1240 psi

@Strain 0.150 %,
Temperature 194 °F
 DAM; ISO 11403-1/-2
8.71 MPa

@Strain 0.230 %,
Temperature 150 °C
 1260 psi

@Strain 0.230 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
8.96 MPa

@Strain 0.110 %,
Temperature 23.0 °C
 1300 psi

@Strain 0.110 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
9.16 MPa

@Strain 0.180 %,
Temperature 90.0 °C
 1330 psi

@Strain 0.180 %,
Temperature 194 °F
 50%RH; ISO 11403-1/-2
9.23 MPa

@Strain 0.440 %,
Temperature 200 °C
 1340 psi

@Strain 0.440 %,
Temperature 392 °F
 DAM; ISO 11403-1/-2
9.51 MPa

@Strain 0.130 %,
Temperature 60.0 °C
 1380 psi

@Strain 0.130 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
9.64 MPa

@Strain 0.220 %,
Temperature 150 °C
 1400 psi

@Strain 0.220 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
9.77 MPa

@Strain 0.0600 %,
Temperature -20.0 °C
 1420 psi

@Strain 0.0600 %,
Temperature -4.00 °F
 DAM; ISO 11403-1/-2