DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Renewably Sourced High Viscosity Polyamide 610 Developed for Extrusion Zytel RS LC3090 NC010 is a renewable sourced polyamide 610 containing a miniumu of 60% renewably sourced ingredient by weight. It is an unreinforced high viscosity gradInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
DAM; ISO 1183
Water Absorption 3.3 %

@Thickness 2.00 mm
 3.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.40 %

@Thickness 2.00 mm
 1.40 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 0.58 %
0.58 %
DAM; Immersion 24h; ASTM D570
Viscosity Test 170 cm³/g
170 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 2.87 MPa

@Strain 0.720 %,
Temperature 90.0 °C
 416 psi

@Strain 0.720 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
2.91 MPa

@Strain 1.12 %,
Temperature 150 °C
 422 psi

@Strain 1.12 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
3.42 MPa

@Strain 0.240 %,
Temperature 23.0 °C
 496 psi

@Strain 0.240 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.52 MPa

@Strain 0.150 %,
Temperature 23.0 °C
 511 psi

@Strain 0.150 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.49 MPa

@Strain 0.180 %,
Temperature 0.000 °C
 651 psi

@Strain 0.180 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
5.82 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 844 psi

@Strain 0.230 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
5.87 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 851 psi

@Strain 0.230 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
6.82 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 989 psi

@Strain 0.250 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
7.64 MPa

@Strain 4.83 %,
Temperature 150 °C
 1110 psi

@Strain 4.83 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
8.73 MPa

@Strain 2.34 %,
Temperature 90.0 °C
 1270 psi

@Strain 2.34 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
11.24 MPa

@Strain 1.36 %,
Temperature 40.0 °C
 1630 psi

@Strain 1.36 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
14.82 MPa

@Strain 0.560 %,
Temperature -20.0 °C
 2149 psi

@Strain 0.560 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
16.03 MPa

@Strain 48.0 %,
Temperature 150 °C
 2325 psi

@Strain 48.0 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
23.07 MPa

@Strain 45.7 %,
Temperature 90.0 °C
 3346 psi

@Strain 45.7 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
25.82 MPa

@Strain 47.28 %,
Temperature 90.0 °C
 3745 psi

@Strain 47.28 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
26.86 MPa

@Strain 1.18 %,
Temperature -40.0 °C
 3896 psi

@Strain 1.18 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
32.38 MPa

@Strain 11.02 %,
Temperature 40.0 °C
 4696 psi

@Strain 11.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
36.08 MPa

@Strain 22.41 %,
Temperature 40.0 °C
 5233 psi

@Strain 22.41 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
42.28 MPa

@Strain 9.84 %,
Temperature 40.0 °C
 6132 psi

@Strain 9.84 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
43.06 MPa

@Strain 8.32 %,
Temperature 23.0 °C
 6245 psi

@Strain 8.32 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
44.96 MPa

@Strain 20.95 %,
Temperature 40.0 °C
 6521 psi

@Strain 20.95 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
47.6 MPa

@Strain 18.65 %,
Temperature 23.0 °C
 6900 psi

@Strain 18.65 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
59.36 MPa

@Strain 3.41 %,
Temperature 23.0 °C
 8609 psi

@Strain 3.41 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
65.29 MPa

@Strain 8.78 %,
Temperature 0.000 °C
 9470 psi

@Strain 8.78 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
65.3 MPa

@Strain 3.17 %,
Temperature -40.0 °C
 9470 psi

@Strain 3.17 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
66.8 MPa

@Strain 3.56 %,
Temperature 0.000 °C
 9690 psi

@Strain 3.56 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
70.39 MPa

@Strain 3.61 %,
Temperature -40.0 °C
 10210 psi

@Strain 3.61 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
73.17 MPa

@Strain 4.99 %,
Temperature -20.0 °C
 10610 psi

@Strain 4.99 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
80.89 MPa

@Strain 4.84 %,
Temperature -20.0 °C
 11730 psi

@Strain 4.84 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
89.79 MPa

@Strain 7.45 %,
Temperature -40.0 °C
 13020 psi

@Strain 7.45 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
90.45 MPa

@Strain 6.44 %,
Temperature -40.0 °C
 13120 psi

@Strain 6.44 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Tensile Modulus 1.20 GPa
174 ksi
50%RH; ISO 527-1/-2
2.30 GPa
334 ksi
DAM; ISO 527-1/-2
Flexural Strength 86.0 MPa
12500 psi
DAM; ISO 178
Flexural Modulus 1.90 GPa
276 ksi
DAM; ISO 178
Secant Modulus 0.137 GPa

@Strain 26.58 %,
Temperature 40.0 °C
 19.8 ksi

@Strain 26.58 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.214 GPa

@Strain 22.41 %,
Temperature 23.0 °C
 31.0 ksi

@Strain 22.41 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.215 GPa

@Strain 20.95 %,
Temperature 40.0 °C
 31.1 ksi

@Strain 20.95 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.294 GPa

@Strain 11.02 %,
Temperature 40.0 °C
 42.6 ksi

@Strain 11.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.430 GPa

@Strain 9.84 %,
Temperature 40.0 °C
 62.3 ksi

@Strain 9.84 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.518 GPa

@Strain 8.32 %,
Temperature 23.0 °C
 75.1 ksi

@Strain 8.32 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.744 GPa

@Strain 8.78 %,
Temperature 0.000 °C
 108 ksi

@Strain 8.78 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
0.826 GPa

@Strain 1.36 %,
Temperature 40.0 °C
 120 ksi

@Strain 1.36 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.988 GPa

@Strain 9.24 %,
Temperature -40.0 °C
 143 ksi

@Strain 9.24 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
1.21 GPa

@Strain 7.63 %,
Temperature -40.0 °C
 175 ksi

@Strain 7.63 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
1.425 GPa

@Strain 0.240 %,
Temperature 23.0 °C
 206.7 ksi

@Strain 0.240 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.47 GPa

@Strain 4.99 %,
Temperature -20.0 °C
 213 ksi

@Strain 4.99 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
1.67 GPa

@Strain 4.84 %,
Temperature -20.0 °C
 242 ksi

@Strain 4.84 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
1.74 GPa

@Strain 3.41 %,
Temperature 23.0 °C
 252 ksi

@Strain 3.41 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.8764 GPa

@Strain 3.56 %,
Temperature 0.000 °C
 272.15 ksi

@Strain 3.56 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
1.95 GPa

@Strain 3.61 %,
Temperature -40.0 °C
 283 ksi

@Strain 3.61 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.06 GPa

@Strain 3.17 %,
Temperature -40.0 °C
 299 ksi

@Strain 3.17 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
2.28 GPa

@Strain 1.18 %,
Temperature -40.0 °C
 330 ksi

@Strain 1.18 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.35 GPa

@Strain 0.150 %,
Temperature 23.0 °C
 340 ksi

@Strain 0.150 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
2.49 GPa

@Strain 0.180 %,
Temperature 0.000 °C
 362 ksi

@Strain 0.180 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
2.53 GPa

@Strain 0.230 %,
Temperature -20.0 °C
 367 ksi

@Strain 0.230 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
2.55 GPa

@Strain 0.230 %,
Temperature -40.0 °C
 370 ksi

@Strain 0.230 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
2.65 GPa

@Strain 0.560 %,
Temperature -20.0 °C
 384 ksi

@Strain 0.560 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2