DuPont Performance Polymers Zytel® ST801AW NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® ST801AW NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® ST801AW NC010 is a Super Tough, high performance polyamide 66 resin. It is UV stabilized and when appropriately colored offers the best resistance to indirect sunlight in automotive interior applications.Information provided by DuPont
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
DAM; ISO 1183
Water Absorption 1.17 %

@Temperature 23.0 °C
 1.17 %

@Temperature 73.4 °F
 DAM; Immersion 24h; ISO 62, Similar to
1.9 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 1.9 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 DAM; Equilibrium 50%RH; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 2.00 mm
 0.020 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Thickness 2.00 mm
 0.018 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
DAM; ISO 2039/2
Tensile Strength at Break 45.0 MPa

@Temperature 23.0 °C
 6530 psi

@Temperature 73.4 °F
 DAM; 50mm/min; ISO 527
48.0 MPa

@Temperature 23.0 °C
 6960 psi

@Temperature 73.4 °F
 50%RH; 50mm/min; ISO 527
Tensile Stress 48.0 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 6960 psi

@Strain 50.0 %,
Temperature 73.4 °F
 50%RH; ISO 527
50.0 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 7250 psi

@Strain 50.0 %,
Temperature 73.4 °F
 DAM; ISO 527
Tensile Strength, Yield 35.5 MPa

@Temperature 23.0 °C
 5150 psi

@Temperature 73.4 °F
 50%RH; ISO 527
49.0 MPa

@Temperature 23.0 °C
 7110 psi

@Temperature 73.4 °F
 DAM; ISO 527
Elongation at Break 44 %

@Temperature 23.0 °C
 44 %

@Temperature 73.4 °F
 DAM; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50%RH; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 DAM; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50%RH; ISO 527
74 %

@Temperature 23.0 °C
 74 %

@Temperature 73.4 °F
 DAM; 50mm/min; ISO 527
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
 DAM; ISO 527
26.5 %

@Temperature 23.0 °C
 26.5 %

@Temperature 73.4 °F
 50%RH; ISO 527
Tensile Modulus 0.775 GPa

@Temperature 23.0 °C
 112 ksi

@Temperature 73.4 °F
 50%RH; ISO 527
1.90 GPa

@Temperature 23.0 °C
 276 ksi

@Temperature 73.4 °F
 DAM; ISO 527
Flexural Modulus 0.728 GPa

@Temperature 23.0 °C
 106 ksi

@Temperature 73.4 °F
 50%RH; ISO 178
1.80 GPa

@Temperature 23.0 °C
 261 ksi

@Temperature 73.4 °F
 DAM; ISO 178
Izod Impact, Notched (ISO) 21.0 kJ/m²

@Temperature -40.0 °C
 9.99 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
77.0 kJ/m²

@Temperature 23.0 °C
 36.6 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 180/1U
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 DAM; ISO 180/1U
Charpy Impact Unnotched 24.0 J/cm²

@Temperature -40.0 °C
 114 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eU
26.0 J/cm²

@Temperature 0.000 °C
 124 ft-lb/in²

@Temperature 32.0 °F
 DAM; ISO 179/1eU
30.0 J/cm²

@Temperature -20.0 °C
 143 ft-lb/in²

@Temperature -4.00 °F
 DAM; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 DAM; ISO 179/1eU
Charpy Impact, Notched 2.10 J/cm²

@Temperature -40.0 °C
 9.99 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
2.20 J/cm²

@Temperature -30.0 °C
 10.5 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
2.20 J/cm²

@Temperature -20.0 °C
 10.5 ft-lb/in²

@Temperature -4.00 °F
 DAM; ISO 179/1eA
2.30 J/cm²

@Temperature -30.0 °C
 10.9 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
3.60 J/cm²

@Temperature 0.000 °C
 17.1 ft-lb/in²

@Temperature 32.0 °F
 DAM; ISO 179/1eA
8.30 J/cm²

@Temperature 23.0 °C
 39.5 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature -40.0 - 23.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ASTM E 831
120 µm/m-°C

@Temperature -40.0 - 23.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
130 µm/m-°C

@Temperature -30.0 - 30.0 °C
 72.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ISO 11359-1/-2
130 µm/m-°C

@Temperature -30.0 - 30.0 °C
 72.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ASTM E 831
140 µm/m-°C

@Temperature 23.0 - 55.0 °C
 77.8 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ASTM E 831
140 µm/m-°C

@Temperature 23.0 - 55.0 °C
 77.8 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ISO 11359-1/-2
170 µm/m-°C

@Temperature 55.0 - 160 °C
 94.4 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ASTM E 831
170 µm/m-°C

@Temperature 55.0 - 160 °C
 94.4 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature -30.0 - 30.0 °C
 61.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ISO 11359-1/-2
110 µm/m-°C

@Temperature -40.0 - 23.0 °C
 61.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ISO 11359-1/-2
110 µm/m-°C

@Temperature -30.0 - 30.0 °C
 61.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 DAM; ASTM E 831
110 µm/m-°C

@Temperature -40.0 - 23.0 °C
 61.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 DAM; ASTM E 831
120 µm/m-°C

@Temperature 55.0 - 160 °C
 66.7 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ASTM E 831
120 µm/m-°C

@Temperature 23.0 - 55.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 131 °F
 DAM; ISO 11359-1/-2
120 µm/m-°C

@Temperature 55.0 - 160 °C
 66.7 µin/in-°F

@Temperature 131 - 320 °F
 DAM; ISO 11359-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+12 ohm-cm

@Temperature 23.0 °C
 2.40e+12 ohm-cm

@Temperature 73.4 °F
 50%RH; IEC 60093
2.50e+16 ohm-cm

@Temperature 23.0 °C
 2.50e+16 ohm-cm

@Temperature 73.4 °F
 DAM; IEC 60093
Surface Resistance 7.10e+12 ohm

@Temperature 23.0 °C
 7.10e+12 ohm

@Temperature 73.4 °F
 50%RH; IEC 60093
2.70e+15 ohm

@Temperature 23.0 °C
 2.70e+15 ohm

@Temperature 73.4 °F
 DAM; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.2

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
3.4

@Frequency 100 Hz,
Temperature 23.0 °C
 3.4

@Frequency 100 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
3.5

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.5

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
6.0

@Frequency 100 Hz,
Temperature 23.0 °C
 6.0

@Frequency 100 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
Dielectric Strength 26.0 kV/mm

@Thickness 2.00 mm,
Temperature 23.0 °C
 660 kV/in

@Thickness 0.0787 in,
Temperature 73.4 °F
 50%RH; IEC 60243-1
26.0 kV/mm

@Thickness 2.00 mm,
Temperature 23.0 °C
 660 kV/in

@Thickness 0.0787 in,
Temperature 73.4 °F
 DAM; IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0050

@Frequency 100 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
0.011

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.011

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 DAM; IEC 60250
0.038

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.038

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
0.176

@Frequency 100 Hz,
Temperature 23.0 °C
 0.176

@Frequency 100 Hz,
Temperature 73.4 °F
 50%RH; IEC 60250
Comparative Tracking Index 600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
 600 V

@Thickness 0.118 in,
Temperature 73.4 °F
 DAM; UL 746A