DuPont™ Surlyn® 9120 Ionomer Resin, Zinc

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer DuPont
Trade Name Surlyn®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Surlyn® 9120 Ionomer Resin, Zinc.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Surlyn® 9120 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade are optimized to deliver exceptional low-temperature toughness. The resin is highly suitable as a polymer modifier, to increase toughness. Surlyn® 9120 can be injection or blow molded, and is processable by extrusion into sheets or shapes.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ASTM D792
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
condition E; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ASTM D2240
Tensile Strength, Ultimate 36.5 MPa
5290 psi
ASTM D638
Tensile Strength, Yield 18.6 MPa
2700 psi
50 mm/min cross speed; ASTM D638
Elongation at Break 345 %
345 %
ASTM D638
Flexural Modulus 0.4275 GPa
62.00 ksi
ASTM D790
Abrasion 1031
1031
NBS Index; ASTM D1630
Thermal Properties Metric English Comments
Melting Point 86.0 °C
187 °F
DSC
Vicat Softening Point 60.0 °C
140 °F
Rate B, ASTM D1525-70