DuPont™ Surlyn® 9650 Ionomer Resin, Zinc

Category	Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer	DuPont
Trade Name	Surlyn®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Surlyn® 9650 Ionomer Resin, Zinc.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Surlyn® 9650 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade are optimized to deliver the toughness of other grades, but with improved injection molding processability.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ASTM D792
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 g/10 min @Load 4.76 lb, Temperature 374 °F	condition E; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	63	63	ASTM D2240
Tensile Strength, Ultimate	22.1 MPa	3210 psi	ASTM D638
Tensile Strength, Yield	12.4 MPa	1800 psi	50 mm/min cross speed; ASTM D638
Elongation at Break	410 %	410 %	ASTM D638
Flexural Modulus	0.220 GPa	31.9 ksi	ASTM D790
Izod Impact, Notched	7.75 J/cm	14.5 ft-lb/in	ASTM D256
Tensile Impact Strength	970 kJ/m²	462 ft-lb/in²	ASTM D1822S
Abrasion	270	270	NBS Index; ASTM D1630

Thermal Properties	Metric	English	Comments
CTE, linear	150 µm/m-°C @Temperature -20.0 - 32.0 °C	83.3 µin/in-°F @Temperature -4.00 - 89.6 °F	ASTM D696
Thermal Conductivity	0.246 W/m-K	1.71 BTU-in/hr-ft²-°F
Melting Point	92.0 °C	198 °F	DTA
Deflection Temperature at 0.46 MPa (66 psi)	48.0 °C	118 °F	ASTM D648
Vicat Softening Point	71.0 °C	160 °F	Rate B, ASTM D1525-70
Brittleness Temperature	-80.0 °C	-112 °F	ASTM D746
Flame Spread	22.9 mm/min	0.902 in/min	ASTM D635

Optical Properties	Metric	English	Comments
Haze	27 % @Thickness 6.40 mm	27 % @Thickness 0.252 in	ASTM D1003A