DuPont™ Tedlar® SP TUA10AH9 Polyvinyl Fluoride Film

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer DuPont
Trade Name Tedlar® SP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Tedlar® SP TUA10AH9 Polyvinyl Fluoride Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
UV Screening, High Gloss. Tedlar® SP polyvinyl fluoride film is designed to provide excellent conformability to substrates while maintaining the good durability, color stability, chemical resistance, and ease of cleaning expected of PVF film. Tedlar® SP also offers custom color capability not previously available in PVF film. Tedlar® SP is an unoriented film. It possesses high elongation and moderate yield stress. After lamination using conventional means, it can be easily embossed and will maintain high pattern definition. Tedlar® SP can also be subjected to high levels of forming without significant recovery stresses.Information provided by DuPont.
Physical Properties Metric English Comments
Thickness 25.4 microns
1.00 mil
Mechanical Properties Metric English Comments
Tensile Strength 41.0 MPa
5950 psi
ASTM D882-80, Method A - 100%
Film Elongation at Break, MD 40 %

@Temperature 20.0 °C
40 %

@Temperature 68.0 °F
110 %

@Temperature 50.0 °C
110 %

@Temperature 122 °F
310 %

@Temperature 75.0 °C
310 %

@Temperature 167 °F
340 %

@Temperature 100 °C
340 %

@Temperature 212 °F
Film Elongation at Break, TD 40 %

@Temperature 20.0 °C
40 %

@Temperature 68.0 °F
110 %

@Temperature 50.0 °C
110 %

@Temperature 122 °F
310 %

@Temperature 75.0 °C
310 %

@Temperature 167 °F
340 %

@Temperature 100 °C
340 %

@Temperature 212 °F
Elongation at Break 200 %
200 %
ASTM D882-80
Tear Strength 550 kN/m
3140 pli
Graves, MD; ASTM D1004
550 kN/m
3140 pli
Graves, TD; ASTM D1004
Film Tensile Strength at Break, MD 11.0 MPa

@Temperature 100 °C
1600 psi

@Temperature 212 °F
18.6 MPa

@Temperature 75.0 °C
2700 psi

@Temperature 167 °F
24.1 MPa

@Temperature 50.0 °C
3500 psi

@Temperature 122 °F
38.6 MPa

@Temperature 20.0 °C
5600 psi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 107 °C
225 °F
Continuous
175 °C
347 °F
Short Cycle
Minimum Service Temperature, Air -72.0 °C
-97.6 °F
Continuous
Shrinkage <= 2.0 %

@Temperature 170 °C
<= 2.0 %

@Temperature 338 °F
ASTM D1204-78
0.45 %

@Temperature 50.0 °C,
Time 1800 sec
0.45 %

@Temperature 122 °F,
Time 0.500 hour
1.5 %

@Temperature 100 °C,
Time 1800 sec
1.5 %

@Temperature 212 °F,
Time 0.500 hour
1.9 %

@Temperature 150 °C,
Time 1800 sec
1.9 %

@Temperature 302 °F,
Time 0.500 hour
Optical Properties Metric English Comments
Haze 1.4 %
1.4 %
Total; Gardner
1.7 %
1.7 %
Internal; Gardner
Gloss 57 %
57 %
20°; Gardner
81 %
81 %
60°; Gardner
93 %
93 %
85°; Gardner
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+13 ohm-cm
4.00e+13 ohm-cm
ASTM D257-78
Dielectric Constant 7.0
7.0
ASTM D151-81
Dielectric Strength 118 kV/mm
3000 kV/in
ASTM D151-81
Dissipation Factor 0.0020
0.0020
ASTM D151-81
Processing Properties Metric English Comments
Processing Temperature 105 - 171 °C
221 - 340 °F
Film Forming Surface Temperature
Descriptive Properties Value Comments
Resistance to Acids No Visible Effect
2 hr Boiling
Resistance to Bases No Visible Effect
Immersion
Weatherability Excellent